一种无卤氮磷复配膨胀型阻燃剂及其制备方法技术

本发明专利技术公开了一种无卤氮磷复配膨胀型阻燃剂及其制备方法，其是以氮磷为主要成分的复合阻燃剂。该产品经过特殊的配方复合和工艺生产，阻燃效果显著，其外观是白色(结晶或无定形)粉末，本身是一种混合物，通过P‑N的协效作用对PP阻燃，阻燃好，热稳定性高，分解温度大于280℃，残炭率高，吸潮性小，具极佳的分散性，化学稳定性好，可与其它物质混合不易起化学变化。

Halogen free nitrogen phosphorus compound intumescent flame retardant and preparation method thereof

The invention discloses a halogen-free nitrogen nitrogen phosphorus compound intumescent flame retardant and a preparation method thereof. The compound flame retardant is composed of nitrogen and phosphorus. The production through special process and formula of compound, flame retardant effect, its appearance is white (crystalline or amorphous powder), itself is a kind of mixture, through the synergistic effect of P N on PP flame retardant, flame retardant, high thermal stability, decomposition temperature greater than 280 DEG C, carbon residue rate, absorption moisture is small, with excellent dispersibility, good chemical stability, can be mixed with other substances is not easy to produce chemical changes.

【技术实现步骤摘要】
一种无卤氮磷复配膨胀型阻燃剂及其制备方法
本专利技术涉及阻燃剂领域，具体为一种无卤氮磷复配膨胀型阻燃剂及其制备方法。
技术介绍
高分子材料因其性能优异、价格低廉而被广泛地应用于国民经济和人民生活的各个领域，2000年仅塑料的生产量即达1.7亿吨，其体积大大超过同年生产的钢材体积。但是大多数高聚物属于易燃、可燃材料，在燃烧时热释放速率大，热值高，火焰传播速度快，不易熄灭，有时还产生浓烟和有毒气体，造成对环境的危害，对人们的生命安全形成巨大的威胁，例如近年来发生火灾频繁，特大火灾伤人事故常有发生，特别是公共场所几次火灾造成重大人员死伤和财产损失，社会影响很大。因此，预防火灾成为人们心中迫切的愿望，如何提高合成高聚物及天然高聚物材料的阻燃性己成为一个急需解决的问题。阻燃剂按照其元素种类可分为：卤系、磷系、卤－磷系、氮系、硅系、铝镁系等，按化学结构分为无机阻燃剂、有机阻燃剂、高分子阻燃剂等，按阻燃剂与被阻燃材料关系分为添加型阻燃剂和反应型阻燃剂。通常在塑料阻燃改性中常采用的方法是添加型阻燃剂共混改性的方法。阻燃作用是通过一个或几个要素来实现的，其中包括六个方面：提高材料热稳定性、捕捉游离基、本文档来自技高网...

【技术保护点】
一种无卤氮磷复配膨胀型阻燃剂，其特征在于，其是由下述重量份的原料制得：聚磷酸铵40‑55,三聚氰胺15‑25，聚戊四醇12‑15，尿酸酯7‑11，无机添加剂5‑10，硼酸锌0.2‑0.4，离子型表面活性剂0.3‑2。

【技术特征摘要】
1.一种无卤氮磷复配膨胀型阻燃剂，其特征在于，其是由下述重量份的原料制得：聚磷酸铵40-55,三聚氰胺15-25，聚戊四醇12-15，尿酸酯7-11，无机添加剂5-10，硼酸锌0.2-0.4，离子型表面活性剂0.3-2。2.根据权利要求1所述的一种无卤氮磷复配膨胀型阻燃剂，其特征在于，无机添加剂指的是氢氧化镁或者氢氧化铝。3.一种如权利要求...

【专利技术属性】
技术研发人员：吴晓静，刘阿钻，李醒醒，李志，
申请(专利权)人：合肥工业大学，
类型：发明
国别省市：安徽,34