一种增强其芯砂退让性和溃散性的一种技术装置制造方法及图纸

本发明专利技术技术公开了一种增强其芯砂退让性和溃散性的一种技术装置，此方法可大大地增强水玻璃砂芯的退让性，大大地提高水玻璃芯砂的溃散性，通过此技术的广泛应用，铸件的裂纹与原来相比较，减少90％以上，同时，由于芯砂的溃散性能得到提高，相同的一个铸件，工人淸砂的劳动强度减少90％，大大提高工作效率。本发明专利技术大大地减少铸件裂纹缺陷的产生，降低了废品率，由于溃散性好清砂容易缩短了生产周期使制造成本低。

An enhanced the core sand collapsibility and collapsibility of a technical device

The invention discloses a technology to enhance its core sand collapsibility and collapsibility of a technical device, this method can greatly enhance the collapsibility of water glass sand core, greatly improve the collapsibility of water glass sand core, through the extensive application of this technology, compared with the original casting cracks, reduced by 90% above, at the same time, due to the increased collapsibility of core sand, a casting the same 90%, reduce labor intensity of workers by sand, greatly improve work efficiency. The invention can greatly reduce the casting crack defects, reduce the rejection rate, due to good collapsibility of sand to shorten the production cycle so that the manufacturing cost is low.

【技术实现步骤摘要】
一种增强其芯砂退让性和溃散性的一种技术装置
本专利技术技术主要涉及铸造水玻璃砂制芯工序，尤其涉及一种增强其芯砂退让性和溃散性的一种技术装置。
技术介绍
现在常用的水玻璃砂制芯工艺，因石英的相变膨胀使包裹在铸件中的砂芯的退让性极差，从而导致铸件的裂纹缺陷较多，轻者返修工作量大重者导致铸件报废，同时，水玻璃砂在高温时极易烧结，给铸件淸砂造成很大的困难，这样就大大地增加了铸件的成本。
技术实现思路
本专利技术的目的在于提供一种增强其芯砂退让性和溃散性的一种技术装置，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种增强其芯砂退让性和溃散性的一种技术装置，包括砂芯、砂芯骨、锯末砂、铁丝网和芯盒，其特征在于，所述的砂芯的外层由骨料和芯砂组成具有一定强度的砂芯表面层，内部用芯砂和低燃点的物料按一定比例混合的混合料打制成的高溃散高退让性的砂芯内层。进一步，所述砂芯的外层中的骨料是一种由金属丝(直径0.5mm-1mm)编织的铁丝网，网眼的尺寸为10X10(mm)。进一步，所述砂芯内层为低燃点的锯末砂。进一步，所述砂芯内层的锯末砂与芯砂的混合比例为体积比1:1。与现有技术相比本文档来自技高网...

【技术保护点】
一种增强其芯砂退让性和溃散性的一种技术装置，包括砂芯、砂芯骨、锯末砂、铁丝网和芯盒，其特征在于，所述的砂芯的外层由骨料和芯砂组成具有一定强度的砂芯表面层，内部用芯砂和低燃点的物料按一定比例混合的混合料打制成的高溃散高退让性的砂芯内层。

【技术特征摘要】
1.一种增强其芯砂退让性和溃散性的一种技术装置，包括砂芯、砂芯骨、锯末砂、铁丝网和芯盒，其特征在于，所述的砂芯的外层由骨料和芯砂组成具有一定强度的砂芯表面层，内部用芯砂和低燃点的物料按一定比例混合的混合料打制成的高溃散高退让性的砂芯内层。2.根据权利要求1所述的增强其芯砂退让性和溃散性的一种技术装置，其特征在于，所述砂芯的外层...

【专利技术属性】
技术研发人员：李勇，杜应流，丁植，
申请(专利权)人：安徽应流集团霍山铸造有限公司，
类型：发明
国别省市：安徽,34