自粘型止水带及生产方法技术
Self adhesive type water stopping belt and producing method
Self adhesive type water stop belt and production method, in order to effectively improve installation efficiency and waterproof performance of water stop belt. A self-adhesive strip, including strip substrate, substrate for both transverse ends of the waterstop sealing, the sealing section of the upper surface and the lower surface coating HMPSA waterproof layer, waterproof layer covering the isolation layer and the formation of the bond. The preparation and use of hot-melt pressure-sensitive adhesive and concrete peeling strength, cohesion is much larger than the existing HMPSA, can form a strong bond with the concrete structure, ensure the waterstop with binding properties and excellent waterproof performance.
【技术实现步骤摘要】
自粘型止水带及生产方法
本专利技术涉及土木工程施工缝的防水技术，特别涉及一种自粘型止水带及生产方法。
技术介绍
地下工程由于施工工艺的需要须留设施工缝，包括纵向水平施工缝与环向垂直施工缝。结合《地下工程防水技术规范》及工程实践，在施工缝中部设置中埋式止水带效果较好。现有的中埋式止水带主要有钢板止水带和橡胶止水带，二者在工程实施和止水效果方面差别较大。钢板止水带易于安装，但止水效果及耐久性能稍欠理想；橡胶类止水带止水效果及耐久性较好，但不易安装。本专利技术止水带能同时弥补上述两种止水带的缺陷，且兼具二者的优点。现有地下工程中常用的施工缝用止水带有钢板止水带或镀锌钢板止水带。但在现实应用中存在下列问题：钢板止水带或镀锌钢板止水带材质刚性较大，施工中便于就位和安装，但由于其和现浇混凝土之间易形成较大宽度的干缩裂缝从而导致渗漏水，止水效果不太理想。钢板止水带在接触带有腐蚀性地下水时，易发生电化学腐蚀，导致钢板产生锈蚀，严重的数年时间即可锈穿腐烂，失去止水效果。镀锌钢板止水带虽在表面镀锌层保护本体钢板，但由于现场试验手段有限，锌层厚度难以检测，且存在若镀锌不均匀或有漏镀点，...
【技术保护点】
自粘型止水带，包括止水带基材(1)，止水带基材(1)的横向两端为止水段(L)，其特征是：所述止水段(L)的上表面、下表面涂覆热熔压敏胶形成防水胶层(2)，防水胶层(2)外覆盖与之形成粘结的隔离层(3)。
【技术特征摘要】
1.自粘型止水带，包括止水带基材(1)，止水带基材(1)的横向两端为止水段(L)，其特征是：所述止水段(L)的上表面、下表面涂覆热熔压敏胶形成防水胶层(2)，防水胶层(2)外覆盖与之形成粘结的隔离层(3)。2.如权利要求1所述的自粘型止水带，其特征是：所述止水带基材(1)为橡胶基材止水带、塑料基材止水带、热塑性弹性体基材止水带、钢边橡胶基材止水带、钢边塑料基材止水带或钢边热塑性弹性体基材止水带中的任意一种。3.如权利要求1所述的自粘型止水带的制备方法，其特征是：所述隔离层(3)为热塑性聚合薄膜。4.如权利要求1至3任意一项所述的自粘型止水带的生产方法，包括如下步骤：①选定止水带基材(1)；②将止水带基材(1)在80～100℃的干燥箱中预热5～10分钟，将热熔压敏胶加热至160～180℃，待其完全熔融后将...