The invention discloses an ultra long carbon chain parent water head hydrophobic monomer used for oil field fracturing fluid and enhanced oil recovery and a preparation method thereof. The technical proposal: (1) 0.2 mol of dibromethane dissolved in acetone, under stirring to two dimethylamino ethyl methacrylate methyl acetone solution adding 0.1 mol, 4 hours to get the N reaction at room temperature, N two methyl ethyl methyl acrylyl ethyl bromide in the body; (2) the intermediate 0.05 mol and 0.055 mol of erucic acid amide propyl two methyl tertiary amine is added to ethanol, methanol at room temperature for 24 hours, get the long carbon chain based hydrophobic monomer parents head. The hydrophobic monomer has strong hydrophobic property and good polymerization activity, the preparation method is simple and the separation is easy, and the hydrophobic monomer has broad application prospect in the oilfield fracturing fluid and the enhanced oil recovery.
【技术实现步骤摘要】
一种超长碳链双亲水头基疏水单体及其制备方法
本专利技术涉及一种油田压裂液及提高采收率用的超长碳链双亲水头基疏水单体及其制备方法。
技术介绍
疏水缔合聚合物是指聚合物分子链上带有少量疏水功能单体的一种水溶性聚合物。由于少量的疏水单体的引入，在聚合物溶液中，疏水单体发生缔合作用，使得聚合物分子发生聚集，形成超分子结构，从而表现出特殊的流变性能，具有良好的增稠、耐温、抗盐、抗剪切等性能，因此受到广泛的关注，并在油田压裂液及提高采收率中大量的应用。疏水缔合聚合物通常采用可聚合的表面活性剂作为疏水单体，采用胶束聚合物得到微嵌段的疏水缔合聚合物。然而常规的疏水单体碳链较短，缔合性能不理想，而且聚合活性较低。为了提高疏水单体的缔合性能，本专利技术采用超长碳链提高疏水单体的缔合性能，但是碳链太长会影响单体的水溶性以及聚合物的水溶性，因此采用双亲水头基同时提高疏水单体的亲水性能，从而制备一种超长碳链双亲水头基可聚合表面活性剂作为疏水缔合聚合物的疏水单体。
技术实现思路
本专利技术的目的：为了提高疏水缔合聚合物的缔合性能及溶解性能，特提供一种超长碳链双亲水头基疏水单体及其制备方法。为了达...
【技术保护点】
一种超长碳链双亲水头基疏水单体及其制备方法，其结构式如下：
【技术特征摘要】
1.一种超长碳链双亲水头基疏水单体及其制备方法，其结构式如下：2.如权利要求1所述一种超长碳链双亲水头基疏水单体及其制备方法，依次包括以下步骤：(1)将0.2摩尔的二溴乙烷溶于丙酮中，在搅拌条件下向丙酮溶液中滴加0.1摩尔的甲基丙烯酸二甲氨基乙酯，在室温下反...
【专利技术属性】
技术研发人员：郑存川，黄志宇，鲁红升，全红平，
申请(专利权)人：西南石油大学，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。