The invention provides a polycarbonate resin composition and molded article containing the polycarbonate resin composition, the polycarbonate resin composition contains a polycarbonate resin (A), phosphorus (B), antioxidants, fatty acid ester (C) and ultraviolet absorber (D), relative to the polycarbonate resin (A) 100 weight, phosphorus (antioxidant B), fatty acid ester (C) and ultraviolet absorber (D) were 0.04 ~ 0.1, 0.03 ~ 0.5 weight weight and 0 to 1 parts by weight, phosphorus containing antioxidants (B) for at least 2 compounds, including 1 kinds of phosphite compounds, phosphite compounds amount phosphorus containing antioxidants (B) a total of 40 to 80 weight%.
【技术实现步骤摘要】
【国外来华专利技术】聚碳酸酯树脂组合物及成形品
本专利技术涉及一种聚碳酸酯树脂组合物及成形品。
技术介绍
聚碳酸酯树脂因其耐冲击性、耐热性、透明性等优异而一直以来被利用于例如导光板、各种透镜、标牌等成形品中。例如专利文献1中公开了一种导光板用芳香族聚碳酸酯树脂组合物，其在重均分子量与数均分子量之比被规定到特定范围的芳香族聚碳酸酯树脂中配合有稳定剂及脱模剂。专利文献2中公开了包含聚碳酸酯、聚甲基丙烯酸甲酯、环状烯烃共聚物等具有高透光率及低双折射性的热塑性树脂的树脂组合物作为导光板用树脂组合物。专利文献3中公开了在聚碳酸酯树脂中配合有聚苯乙烯及1种磷系抗氧化剂的光学用成形品用聚碳酸酯树脂组合物。专利文献4中公开了一种导光构件用聚碳酸酯树脂组合物，其在具有特定粘均分子量的芳香族聚碳酸酯树脂中配合有2种亚磷酸酯系稳定剂及脂肪酸酯，一种亚磷酸酯系稳定剂具有特定结构，且其量比另一种亚磷酸酯系稳定剂少。然而，近年来，对光学用成形品不仅要求透光率而且要求兼具例如热稳定性、机械强度、色调、亮度、挤出成形性、耐候性、长期可靠性等各种特性中与其用途相应的特性，专利文献1～4中公开的树脂组合物并不能充分满足...
【技术保护点】
一种聚碳酸酯树脂组合物，其含有聚碳酸酯树脂(A)、磷系抗氧化剂(B)、脂肪酸酯(C)和紫外线吸收剂(D)而成，所述磷系抗氧化剂(B)的量相对于所述聚碳酸酯树脂(A)100重量份为0.04～0.1重量份，所述脂肪酸酯(C)的量相对于所述聚碳酸酯树脂(A)100重量份为0.03～0.5重量份，所述紫外线吸收剂(D)的量相对于所述聚碳酸酯树脂(A)100重量份为0～1重量份，所述磷系抗氧化剂(B)为至少2种化合物，该至少2种化合物中的1种为通式(1)所示的化合物，
【技术特征摘要】
【国外来华专利技术】2015.02.10 JP 2015-024071;2015.03.10 JP 2015-047171.一种聚碳酸酯树脂组合物，其含有聚碳酸酯树脂(A)、磷系抗氧化剂(B)、脂肪酸酯(C)和紫外线吸收剂(D)而成，所述磷系抗氧化剂(B)的量相对于所述聚碳酸酯树脂(A)100重量份为0.04～0.1重量份，所述脂肪酸酯(C)的量相对于所述聚碳酸酯树脂(A)100重量份为0.03～0.5重量份，所述紫外线吸收剂(D)的量相对于所述聚碳酸酯树脂(A)100重量份为0～1重量份，所述磷系抗氧化剂(B)为至少2种化合物，该至少2种化合物中的1种为通式(1)所示的化合物，式中，R1表示碳数1～20的烷基，a表示0～3的整数，所述通式(1)所示的化合物的量为磷系抗氧化剂(B)总量的40～80重量％。2.根据权利要求1所述的聚碳酸酯树脂组合物，其中，通式(1)所示的化合物为亚磷酸...
【专利技术属性】
技术研发人员：长尾厚史，木田惠里子，中石英二，
申请(专利权)人：住化PC有限公司，
类型：发明
国别省市：日本,JP