Resin lens and other optical components of the present invention provides resin composition and molding the composition and optical components, the resin composition has comparable glass high pencil hardness, and bending strength is excellent, and can provide a cured mold suitable for mold forming with excellent releasability. Resin composition for optical components of the present invention comprises 15 to 65 parts by weight of silsesquioxane derivatives (a), and the (a) component for a total amount of 100 parts by weight of a skeleton containing an alicyclic epoxy resin (b), and 0.01 to 5 parts by weight of the curing agent. Silsesquioxane derivatives (a) with 2 (3,4 epoxycyclohexyl) hydrolysis condensation product of three alkoxy silane ethylene, which has 2 (3,4 epoxycyclohexyl) ethyl, weight average molecular weight is 2000 ~ 10000, for ladder type structure and / or random type structure.
【技术实现步骤摘要】
【国外来华专利技术】光学部件用树脂组合物
本专利技术涉及光学部件用树脂组合物，更详细地说，涉及能够适合地用于照相机模块等中的含有倍半硅氧烷衍生物的树脂组合物，特别涉及弯曲强度优异而且具有高铅笔硬度、适于树脂透镜等树脂制光学部件的组合物。
技术介绍
在智能手机、数码照相机、或者车载照相机、近接传感器等车载光学传感器等中，摄像功能通常利用将透镜安装于CCD或CMOS等图像传感器而成的照相机模块来达成。在这样的照相机模块中，使用树脂透镜。以往，作为树脂透镜的材料，使用脂环式聚烯烃树脂等热塑性透明树脂，树脂透镜是将它们注射成型为透镜形状而制造的。近年来，从削减电子设备的安装成本的方面出发，强烈期望着能够适应于照相机模块安装中的回焊工序的透镜材料，作为耐热性的树脂透镜，在专利文献1中公开了对于将笼型结构的聚有机倍半硅氧烷作为主成分的有机硅树脂固化而成的透镜。另外，在专利文献2中公开了将含有脂环式环氧基的笼型结构的倍半硅氧烷和含有芳香环的环氧树脂用于透镜等光学用途中。但是，这些有机硅树脂的弯曲强度不充分。与此相对，在专利文献3中，为了实现具有耐热性、同时弯曲强度也优异的树脂制光学部件，公开了含有...
【技术保护点】
一种光学部件用树脂组合物，该树脂组合物含有15重量份～65重量份的倍半硅氧烷衍生物(a)、与上述(a)成分的合计量为100重量份的含有脂环式骨架的环氧树脂(b)、以及0.01重量份～5重量份的固化剂，上述倍半硅氧烷衍生物(a)是具有2‑(3,4‑环氧环己基)乙基的三烷氧基硅烷的水解‑缩合物，其具有2‑(3,4‑环氧环己基)乙基，重均分子量为2000～10000，为梯型结构和/或无规型结构。
【技术特征摘要】
【国外来华专利技术】2014.11.12 JP 2014-2297311.一种光学部件用树脂组合物，该树脂组合物含有15重量份～65重量份的倍半硅氧烷衍生物(a)、与上述(a)成分的合计量为100重量份的含有脂环式骨架的环氧树脂(b)、以及0.01重量份～5重量份的固化剂，上述倍半硅氧烷衍生物(a)是具有2-(3,4-环氧环己基)乙基的三烷氧基硅烷的水解-缩合物，其具有2-(3,4-环氧环己基)乙基，重均分子量为2000～10000，为梯型结构和/或无规型结构。2.如权利要求1所述的树脂组合物，其中，上述三烷氧基硅烷为选自由2-(3,4-环氧)环己基乙基三甲氧基硅烷和2-(3,4-环氧)环己基乙基三乙氧基硅烷组成的组中的至少一...