制造基于硫化物的陶瓷元件的方法，特别是用于IR光学应用技术
A method of manufacturing a sulfide based ceramic element, especially for IR optical applications
The invention discloses a method for manufacturing ceramic components such as sulfide transparent infrared based on optical element, which comprises the following steps: synthesis of sulfide powder; and sintering the powder to form the ceramic element; which is characterized in that the steps of the synthesis of the sulfide powder by combustion in aqueous solution for the solution containing water as the only solvent, or containing water as the main solvent, and the solvent contains up to 10% of total quality, preferably up to 1% of one or more other solvents. The sulfide powder may be particularly selected from ZnS, BaLa2S4, and CaLa2S4.
【技术实现步骤摘要】
【国外来华专利技术】制造基于硫化物的陶瓷元件的方法，特别是用于IR光学应用本专利技术涉及一种制造基于硫化物的陶瓷元件的方法，更具体地涉及一种用于红外光学应用的在红外线中透明的基于硫化物的陶瓷元件。对于军事和民用的一些应用，需要在电磁波谱的红外部分，特别是在中和远红外线(波长大于或等于3μm)中显示出良好透明性的材料。它们可以用作激光基质材料，或用于制造热相机、夜视系统、导弹引导头等的窗口、透镜或其他用于激光的光学元件。氧化物和氟化物已经作为在近红外(1-3μm)中选择的材料出现；硫族化物玻璃和锗晶体用于8-12μm窗口的中红外线，而基于硫化物的陶瓷，尤其是ZnS、BaLa2S4和CaLa2S4在更大的波长下是非常有前景的。ZnS目前已经在军事应用中使用。用于光学应用的基于硫化物的(特别是ZnS)材料目前通过化学气相沉积(CVD)制造，参见例如D.C.Harris，MaterialsforInfraredWindowsandDomes，PropertiesandPerformance，EditedbySPIE-TheInternationalSocietyforOpticalEngine...
【技术保护点】
制造基于硫化物的透明红外光学陶瓷元件的方法，其包括以下步骤：‑合成硫化物粉末；和‑烧结所述粉末以形成所述陶瓷元件；其特征在于，所述合成所述硫化物粉末的步骤通过在水溶液中燃烧来进行，所述溶液包含水作为其唯一的溶剂，或含有水作为其主溶剂，并且包含溶剂总质量的至多10％，优选至多1％的一种或多种其他溶剂。
【技术特征摘要】
【国外来华专利技术】2014.07.10 EP 14176610.51.制造基于硫化物的透明红外光学陶瓷元件的方法，其包括以下步骤：-合成硫化物粉末；和-烧结所述粉末以形成所述陶瓷元件；其特征在于，所述合成所述硫化物粉末的步骤通过在水溶液中燃烧来进行，所述溶液包含水作为其唯一的溶剂，或含有水作为其主溶剂，并且包含溶剂总质量的至多10％，优选至多1％的一种或多种其他溶剂。2.根据前述权利要求的方法，其中所述硫化物粉末选自ZnS、BaLa2S4和CaLa2S4。3.根据前述权利要求中任一项所述的方法，其中所述合成所述硫化物粉末的步骤包括制备含金属的氧化剂和含硫的有机燃料的水溶液，并加热所述溶液以引发燃烧反应。4.根据权利要...
【专利技术属性】
技术研发人员：N·阿克梅赫，O·梅尔德里格诺科纳内克，XH·张，
申请(专利权)人：国立科学研究中心，雷恩第一大学，
类型：发明
国别省市：法国,FR