The invention discloses a cable high flame resistance and corrosion resistance of the PVC formula, which is characterized in that made of the following raw materials in weight portion: 20 flame retardant polyethylene DOP material 20 80 copies, 40 copies, 40 copies of EVA15, Zinc Oxide 2 7, six three 6 phosphoryl methyl amine 8 a 1 anti granule 2, chlorinated paraffin 2 3 copies, 1.3 copies of 0.5 additives. The beneficial effect of the invention is that the PVC pipe made by the formula can enhance the impact resistance, strength, plasticity, softness, fire resistance and corrosion resistance, and is relatively low, and is suitable for popularization and application.
【技术实现步骤摘要】
一种高阻燃性、耐腐蚀性的电缆用PVC配方
本专利技术涉及塑胶管道
,具体涉及一种高阻燃性、耐腐蚀性的电缆用PVC配方。
技术介绍
PVC管材的主要成分是聚氯乙烯,另外加入其它成分来增强其耐热性、韧性、延展性等。PVC在当今世界上深受喜爱,是颇为流行并广泛应用的一种合成材料。PVC管材是一种成熟的管材,主要应用于给排水工程。PVC管材具有耐酸、耐碱、耐腐蚀、强度高等优点,但抗冲性能比较差。
技术实现思路
本专利技术提供一种高阻燃性、耐腐蚀性的电缆用PVC配方,利用该配方制造出来的PVC管材可以增强抗冲性能及强度。为达到上述目的,本专利技术一种高阻燃性、耐腐蚀性的电缆用PVC配方,其特征在于由下列重量份的原料制成:阻燃聚乙烯20-80份,DOP材料20-40份,EVA15-40份,氧化锌2-7份,六甲基磷酰三胺6-8份,抗冲剂1-2份,氯化石蜡2-3份,助剂0.5-1.3份。作为优选,由下列最优配比原料制成:阻燃聚乙烯60份,DOP材料30份,EVA30份,氧化锌4份,六甲基磷酰三胺7份,抗冲剂1.4份,氯化石蜡2.6份,助剂0.6份。作为优选,助剂为增塑剂、润湿剂、稳定剂中的一种或两种以上组成。本专利技术的有益效果是:利用该配方制造出来的PVC管材可以增强抗冲性能及强度、热塑性、柔软性、阻燃性和耐腐蚀性,而且成比较低,适合推广应用。具体实施方式以下对本专利技术的优选实施例进行说明,应当理解,此处所描述的优选实施例仅用于说明和解释本专利技术,并不用于限定本专利技术。实施例1本专利技术一种高阻燃性、耐腐蚀性的电缆用PVC配方,由下列重量份的原料制成:阻燃聚乙烯 ...
【技术保护点】
一种高阻燃性、耐腐蚀性的电缆用PVC配方,其特征在于由下列重量份的原料制成:阻燃聚乙烯20‑80份,DOP材料20‑40份,EVA15‑40份,氧化锌2‑7份,六甲基磷酰三胺6‑8份,抗冲剂1‑2份,氯化石蜡2‑3份,助剂0.5‑1.3份。
【技术特征摘要】
1.一种高阻燃性、耐腐蚀性的电缆用PVC配方,其特征在于由下列重量份的原料制成:阻燃聚乙烯20-80份,DOP材料20-40份,EVA15-40份,氧化锌2-7份,六甲基磷酰三胺6-8份,抗冲剂1-2份,氯化石蜡2-3份,助剂0.5-1.3份。2.如权利要求1所述的一种高阻燃性、耐腐蚀性的电缆用PV...