The invention provides a composite of recycled plastics and its preparing method, prepared from the following raw materials: the mass percentage of waste polyethylene 80 ~ 90%, 4 ~ 8% straw powder, calcium carbonate modified by 2 ~ 10%, 0.1 ~ 1%, silane coupling agent styrene butadiene styrene copolymer 2 ~ 4% and 0.2 ~ 0.6% crosslinking agent. Preparation method: 1) with hot water will boil straw powder treated for 5 ~ 10min, cooling to room temperature and then filtered to obtain the straw powder; 2) step 1) treated straw powder and waste polyethylene, modified calcium carbonate, silane coupling agent, styrene butadiene styrene copolymer and crosslinking agent in high speed condition mixed, prepared mixed material; 3) using a double screw extruder, the mixture material extruded. The recycled plastic has the advantages of high strength and good stability.
【技术实现步骤摘要】
复合再生塑料及其制备方法
本专利技术属于废旧塑料回收利用
，具体涉及一种复合再生塑料及其制备方法。
技术介绍
随着塑料行业的迅猛发展，聚乙烯作为一种通用塑料，广泛应用于日用品、建筑、汽车制造业等领域。特别在管材领域，由于聚乙烯管材具有柔韧性好、耐腐蚀、易施工和安装等特点，广泛应用于市政和建筑给排水、燃气、供热采暖、电线电缆穿线、农用节水灌溉和工业排污、矿山矿物输送等领域。目前，PE管材已成为继PVC之后，世界上消费量第二大的塑料管道品种。随着聚乙烯应用领域的扩大和使用量的增加，废旧聚乙烯也与日俱增。废旧聚乙烯由于发生老化降解，其物理性能远不及新料聚乙烯，它的应用也受到了极大的限制，只能用于制作低性能的产品。若不加以应用，浪费资源，又会对环境造成极大的污染。废旧聚乙烯的再生使用，有利于塑料行业的可持续发展。综上所述，废旧聚乙烯的再生具有重要的社会意义和经济意义。公开号为CN101851363A公开了一种废旧聚乙烯的再生方法。通过将废旧聚乙烯、交联剂、纳米材料在双螺杆挤出机中交联、原位增强，得到熔融状态的再生聚乙烯。该专利技术通过交联和使用纳米材料提高再生料的强...
【技术保护点】
一种复合再生塑料，其特征在于，由以下质量百分比的原料制成：废旧聚乙烯80～90％、秸秆粉4～8％、改性碳酸钙2～10％、硅烷偶联剂0.1～1％、苯乙烯‑丁二烯‑苯乙烯共聚物2～4％以及交联剂0.2～0.6％。
【技术特征摘要】
1.一种复合再生塑料，其特征在于，由以下质量百分比的原料制成：废旧聚乙烯80～90％、秸秆粉4～8％、改性碳酸钙2～10％、硅烷偶联剂0.1～1％、苯乙烯-丁二烯-苯乙烯共聚物2～4％以及交联剂0.2～0.6％。2.根据权利要求1所述的复合再生塑料，其特征在于，改性碳酸钙的制备方法：将碳酸钙置于高速混合机中进行搅拌，然后把含有5～15wt％的马来酸的丙酮溶液滴加到高速混合机中，在90～100℃下中混合5～10min，改性后的碳酸钙置于烘箱中直至恒重，得到表面改性碳酸钙。3.根据权利要求1所述的复合...
【专利技术属性】
技术研发人员：鲁伟，李娟，
申请(专利权)人：安徽国登管业科技有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。