The invention discloses a method for processing single crystal rework sheet, comprises the following steps: (1) the rework sheet sorting out, not in source diffusion furnace, high temperature treatment; (2) the rework sheet after high temperature treatment in deionized water by ultrasonic cleaning or alkaline treatment at room temperature (; 3) last step (2) been cleaned rework process in the wool wool groove; (4) spray film will rework after wool making, then placed in the mixed solution of hydrofluoric acid and hydrochloric acid for pickling treatment, followed by rinsing and drying. The invention can reduce the quantity of the rework piece in the production process of the battery sheet, and improve the conversion efficiency and the yield of the rework piece.
【技术实现步骤摘要】
一种处理单晶返工片的方法
本专利技术属于太阳能电池制造
，特别是指一种处理单晶返工片的方法。
技术介绍
随着化石能源的不断减少和环境污染的不断加剧，新能源的研发与推广使用得到高度关注。其中，太阳能作为新能源之一，其丰富、洁净等优点使其最可能成为新能源的主导。目前，在众多种类的太阳能电池中，晶硅太阳能电池已经成为主导，提高电池的转换效率和降低成本是我们研究的热点。目前产业化的晶硅太阳能电池片的制造工艺包括制绒、扩散、刻蚀、去PSG、PECVD、丝网印刷、烧结、分类检测。在晶硅太阳能电池的生产工艺中，制绒工序使硅片表面织构化形成随机分布的金字塔结构的绒面或者类似于半球状的凹陷等不同表面形状，是有效地降低表面反射率的方法之一，提高太阳能电池表面的光吸收，达到提高其转换效率的目的。在制绒工序中，经常会出现碎片率高、色斑、花篮印等异常现象，影响生产效率，降低转换效率甚至导致降级或报废，增加生产成本。本专利技术中采用一种晶硅制绒后色斑片的返工处理方法，有效地降低因色斑片引起的降级或报废的数量，降低了生产成本。其中清洗制绒工序返工片类型主要包括：油污片、手印片、白斑片、局...
【技术保护点】
一种处理单晶返工片的方法，其特征在于，包括以下步骤，(1)将返工片分选出来，置于不通源的扩散炉中，进行高温处理，温度为1000±1℃高温处理时间为15～20min；(2)将高温处理后的返工片放入去离子水中在常温下进行超声波清洗或碱洗处理，超声波清洗的频率是20‑50KHZ，功率是 1800W，清洗时间 2～ 10min；(3)当制绒槽内的溶液为刚失效的溶液时，先将制绒槽内的溶液排掉 1/3，然后注入等量纯水稀释溶液，然后在溶液内补加添加剂、NaOH 和异丙醇，控制每升稀释后的溶液加入1.25mL 添加剂，6.3g NaOH，8mL 异丙醇；最后将步骤（2）得到的返工片在上述...
【技术特征摘要】
1.一种处理单晶返工片的方法，其特征在于，包括以下步骤，(1)将返工片分选出来，置于不通源的扩散炉中，进行高温处理，温度为1000±1℃高温处理时间为15～20min；(2)将高温处理后的返工片放入去离子水中在常温下进行超声波清洗或碱洗处理，超声波清洗的频率是20-50KHZ，功率是1800W，清洗时间2～10min；(3)当制绒槽内的溶液为刚失效的溶液时，先将制绒槽内的溶液排掉1/3，然后注入等量纯水稀释溶液，然后在溶液内补加添加剂、NaOH和异丙醇，控制每升稀释后的溶液加入1.25mL添加剂，6.3gNaOH，8m...
【专利技术属性】
技术研发人员：蒋建宝，
申请(专利权)人：无锡赛晶太阳能有限公司，
类型：发明
国别省市：江苏,32