The invention discloses a high biocompatibility of fluorine rubber formula, which is based on the fluorine rubber reclaimed rubber as the main raw materials, including the following components: fluorine rubber reclaimed rubber 70 ~ 85 fluorine rubber gum 15 ~ 30; 1 to 5 portions of phosphatidyl choline; calcium hydroxide 5 ~ 8 ~ 7; carbon black 15; 0.2 to 1 portions of stearic acid; zinc stearate 1 ~ 3; two 1 dioctyl - 3; Brazil 2 La - 5; 3, 2 to 8 portions of vulcanizing agent; the components by weight. According to the high compatibility fluorine rubber formula obtained by the invention, the fluorine rubber waste material and leftover material can be effectively recovered, and the property of the regenerated fluorine rubber produced by the utility model meets the technical requirement, and the cost is lower and the environment is more environmentally friendly.
【技术实现步骤摘要】
一种高生物相容性的氟橡胶配方
本专利技术属于改性氟橡胶
，尤其涉及氟橡胶的边角料、废胶等回收再利用技术。
技术介绍
氟橡胶是一种具有优良弹性的橡胶材料。但它的材料成本高，因而对加工过程中产生的胶边、废品制成的氟橡胶再生胶生产氟橡胶板，进行资源再生利用，使其能重复加工利用，具有广阔的市场前景和良好的环境保护作用。
技术实现思路
专利技术目的：针对上述现有存在的问题和不足，本专利技术的目的是提供了一种高生物相容性的氟橡胶配方，能有效回收利用氟橡胶边角料和氟橡胶废料等制成的氟橡胶再生胶，降低氟橡胶成本的同时能保护环境。技术方案：为实现上述专利技术目的，本专利技术采用以下技术方案：一种高生物相容性的氟橡胶配方，它是以氟胶再生胶为主原料，包括以下组分：氟胶再生胶70～85份氟橡胶原胶15～30份；磷脂胆碱1～5份；氢氧化钙5～8份；炭黑7～15份；硬脂酸0.2～1份；硬脂酸锌1～3份；二辛脂1～3份；巴西腊2～5份；3号硫化剂2～8份；上述组分均以重量份数计。上述组分均以重量份数计。作为优选，各组分含量如下：氟胶再生胶80份；氟橡胶260320份；磷脂胆碱3份；氢氧化钙6...
【技术保护点】
一种高生物相容性的氟橡胶配方，它是以氟胶再生胶为主原料，包括以下组分： 氟胶再生胶 70～85份 氟橡胶原胶 15～30份； 磷脂胆碱 1～5份； 氢氧化钙 5～8份； 炭黑 7～15份； 硬脂酸 0.2～1份； 硬脂酸锌 1～3份； 二辛脂 1～3份； 巴西腊 2～5份； 3号硫化剂 2～8份； 上述组分均以重量份数计。
【技术特征摘要】
1.一种高生物相容性的氟橡胶配方，它是以氟胶再生胶为主原料，包括以下组分：氟胶再生胶70～85份氟橡胶原胶15～30份；磷脂胆碱1～5份；氢氧化钙5～8份；炭黑7～15份；硬脂酸0.2～1份；硬脂酸锌1～3份；二辛脂1～3份；巴西腊2～5份；3号硫化剂2～8份；上述组分均以重量份数计。2.根据权利要求1所述高生物相容性的氟橡胶配方，其...