The invention discloses a lock panel and the plastic combination process of metal, concrete steps are as follows: step one, the metal lock panel is placed in plastic mould; step two, the plastic particles are loaded into the injection molding machine and melting plastic particles melt by pressure injection plastic mold, cooling to room temperature and time plastic coated on the metal surface of the lock panel; step three, surface treatment can be finished in the plastic surface. In the process of metal surface before the lock panel is coated with a layer of plastic, and then when the surface treatment on the plastic surface is relatively simple, simple preparation process, low production cost, and the other can be more diversified (according to different molding, low cost), in on plastic surface treatment gloss were relatively higher. The anti chloride corrosion and not finished, will not rust, can satisfy the needs of customers.
【技术实现步骤摘要】
一种金属锁面板与塑料的结合工艺
本专利技术涉及锁领域，具体是一种金属锁面板与塑料的结合工艺。
技术介绍
锁具是日常生活中常见的物品，是指起封闭作用的器具，它包括锁、钥匙及其附件，一般解释为“必须用钥匙方能开脱的封缄器”。随着人们生活水平的提高，人们的防范意识的加强，人们在自己的家门上安装锁具，其他人就打不开该锁具，也就拿不走住宅内的物品，避免财产损失。锁面板是锁的最外侧的部件，现有锁面板基本都是以金属材质为主，在金属材质上面进行表面处理(硫化、电镀、喷漆、抛光等)，工序及成本相对较高，且时间久了容易氧化生锈腐蚀，造成锁面板不美观。
技术实现思路
本专利技术的目的在于提供一种金属锁面板与塑料的结合工艺，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种金属锁面板与塑料的结合工艺，具体步骤如下：步骤一，将金属锁面板放置在塑料模具中；步骤二，将塑料颗粒装入注塑机中并且熔融，将熔融的塑料颗粒利用压力注进塑料模具中，冷却至常温，此时塑料包裹在金属锁面板的表面；步骤三，在塑料表面进行表面处理即可得到成品。作为本专利技术进一步的方案：步骤三的表面处理包括硫化、电镀、喷漆和抛光处理。作为本专利技术进一步的方案：步骤二中的注塑时间与冷却时间之比为1:9-17。与现有技术相比，本专利技术的有益效果是：本工艺在金属锁面板表面先覆一层塑料，然后在塑料表面进行表面处理的时候就相对简单，制备工艺简单，生产成本低，而且造型可以更加多样化(可根据不同模具成型，成本低)，在塑料上面进行表面处理的光泽度等都相对较高，得到的成品抗氯化、不会腐蚀并且不会生锈，可以满足人...
【技术保护点】
一种金属锁面板与塑料的结合工艺，其特征在于，具体步骤如下：步骤一，将金属锁面板放置在塑料模具中；步骤二，将塑料颗粒装入注塑机中并且熔融，将熔融的塑料颗粒利用压力注进塑料模具中，冷却至常温，此时塑料包裹在金属锁面板的表面；步骤三，在塑料表面进行表面处理即可得到成品。
【技术特征摘要】
1.一种金属锁面板与塑料的结合工艺，其特征在于，具体步骤如下：步骤一，将金属锁面板放置在塑料模具中；步骤二，将塑料颗粒装入注塑机中并且熔融，将熔融的塑料颗粒利用压力注进塑料模具中，冷却至常温，此时塑料包裹在金属锁面板的表面；步骤三，在塑料表面进行表面处...