The invention relates to the technical field of shutter curtain, in particular to a composite material of a shutter curtain blade and a method for preparing the shutter curtain blade. A shutter blade of composite material provided by the invention comprises the following components by weight: PS 60 ~ 70, 10 to 20 portions of talcum powder, PC 10 ~ 20, 1 ~ 2 phr plasticizer, anti UV agent 0.5 ~ 1, crosslinking agent 0.1 ~ 0.2 and 0.1 ~ 0.2 pigment. The shutter blade composite material of the invention the use of polymer materials, louver blades made of the composite material has high strength, not easy to warp, excellent performance is not easy broken, and has the properties of anti ultraviolet aging.
【技术实现步骤摘要】
一种百叶窗帘叶片复合材料及其制备所述百叶窗帘叶片的方法
本专利技术涉及窗帘
，具体涉及一种百叶窗帘叶片复合材料及其制备所述百叶窗帘叶片的方法。
技术介绍
现有技术的百叶窗帘的叶片通常采用单一组分的塑胶、木条、金属等单一材料制成，采用单一材料制成的百叶窗帘叶片常常会出现翘曲、强度低、易折损的现象发生，且现有技术的百叶窗叶片往往不具备抗紫外光老化的性能。
技术实现思路
为了解决现有的百叶窗帘叶片的上述问题，本专利技术提供一种百叶窗帘叶片复合材料及其制备所述百叶窗帘叶片的方法。本专利技术的百叶窗帘的叶片采用高分子复合材料制成，具有良好的平整度、良好的抗折性能及良好的抗紫外光的性能。本专利技术提供的一种百叶窗帘叶片复合材料，包括按重量份数计的如下组分：PS60～70份，滑石粉10～20份，PC10～20份，增塑剂1～2份，抗紫外剂0.5～1份，交联剂0.1～0.2份和颜料0.1～0.2份。优选地，所述增塑剂为邻苯二甲酸二(2-乙基己)酯。优选地，所述抗紫外剂为二氧化钛。优选地，所述交联剂为二异氰酸酯。用所述百叶窗帘叶片复合材料制备百叶窗帘叶片，包括以下步骤：步骤一：称量...
【技术保护点】
一种百叶窗帘叶片复合材料，其特征在于，包括按重量份数计的如下组分：PS 60～70份，滑石粉10～20份，PC 10～20份，增塑剂1～2份，抗紫外剂0.5～1份，交联剂0.1～0.2份和颜料0.1～0.2份。
【技术特征摘要】
1.一种百叶窗帘叶片复合材料，其特征在于，包括按重量份数计的如下组分：PS60～70份，滑石粉10～20份，PC10～20份，增塑剂1～2份，抗紫外剂0.5～1份，交联剂0.1～0.2份和颜料0.1～0.2份。2.根据权利要求1所述的百叶窗帘叶片复合材料，其特征在于：所述增塑剂为邻苯二甲酸二(2-乙基己)酯。3.根据权利要求1所述的百叶窗帘叶片复合材料，其特征在于：所述抗紫外剂为二氧化钛。4.根据权利要求1所述的百叶窗帘叶片复合材料，其特征在于：所述交联剂为二异氰酸酯。5.用权利要求1～4中任一项所述百叶窗帘叶片复合...