The present invention provides a method for producing iron ore slag foaming brick, raw materials form to break through the traditional brick, a reasonable ratio by using iron powder residue, loess mud and foam, forming the brick material, and then take the appropriate firing process, and ultimately made foam brick, foaming polymer foam after combustion make iron powder residue with loess mud after firing will form a porous or internal multi bubble structure, low density, and can completely replace the traditional foam bricks, and the invention can be applied to higher strength, more pressure in complex environment; at the same time can consume a large amount of iron powder residue, effectively solve the problem of the accumulation of waste slag, waste utilization and reduce environmental pollution and consumption, waste utilization and solve the problem of the accumulation of waste slag has obvious effect.
【技术实现步骤摘要】
一种生产铁精粉废渣发泡砖的方法
本专利技术涉及制砖领域，具体涉及一种生产铁精粉废渣发泡砖的方法。
技术介绍
发泡砖烧制工艺已为公知，如中国专利技术专利CN201410581006.2公开一种轻质泡沫砖，其是由下述重量份的原料制得：废玻璃30-40，浮石粉10-15，蛭石粉5-10，陶砂5-10，海泡石粉4-6，氢氧化钙5-10，硅酸钙1-2，草酸0.5-1，聚乙二醇2-4，水溶性羊毛脂1-2，水玻璃1-2，石油磺酸钡1-2，月桂醇聚醚硫酸酯钠2-4，羟乙基纤维素1-2，复合填料5-10，水40-60；所述复合填料由下列重量份的原料制成：麦饭石粉10-15，高岭土10-15，糯米粉5-10，竹炭粉5-10，维生素C磷酸酯镁1-2，水杨酸钠1-2，羟丙基二淀粉磷酸酯0.5-1，酒石酸钾钠2-4，聚丙烯酸钠0.5-1，麦芽糖醇1-2；所述复合填料的制备方法是：将麦饭石粉、高岭土、酒石酸钾钠和麦芽糖醇混合后研磨均匀，200-300℃处理1-2h，用水反复洗涤后加入糯米粉、竹炭粉和适量水60-80℃搅拌0.5-1h，冷却至常温，加入其余原料继续搅拌10-15min，干燥后研...
【技术保护点】
一种生产铁精粉废渣发泡砖的方法，其特征在于，包括如下步骤：(1)将铁精粉废渣和黄土泥按照体积份数比60‑80：20‑40混合在一起；(2)加适量水进行搅拌制成均匀且吸水饱和的混合物A；(3)在混合物A中加入适量发泡物进行搅拌至均匀；(4)制成砖坯；(5)烧制成成品砖。
【技术特征摘要】
1.一种生产铁精粉废渣发泡砖的方法，其特征在于，包括如下步骤：(1)将铁精粉废渣和黄土泥按照体积份数比60-80：20-40混合在一起；(2)加适量水进行搅拌制成均匀且吸水饱和的混合物A；(3)在混合物A中加入适量发泡物进行搅拌至均匀；(4)制成砖坯；(5)烧制成成品砖。2.根据权利要求1所述的一种生产铁精粉废渣发泡砖的方法，其特征在于：在上述步骤(3)中，若加入的发泡物为吸水发泡物，在加入发泡物之前，先在混合物A中加入占混合物A体积20-30％的水，然后加入适量发泡物进行搅拌至均匀；若加入的发泡物为不吸水发泡物，则直接在混合物A中加入适量发泡物进行搅拌至均匀。3.根据权利要求2所述的一种生产铁精粉废渣发泡砖的方法，其特征在于：在...
【专利技术属性】
技术研发人员：郭霏霏，傅贵华，郭献忠，吴丽萍，
申请(专利权)人：泉州理工职业学院，
类型：发明
国别省市：福建,35