The invention discloses a method for preparing a core shell type nickel oxide / nickel photocatalyst. The method comprises the following steps: 1 ~ 4G sixteen alkyl three methyl bromide 20mL dissolved in toluene, adding 4 ~ 5g 80 ~ 100 mesh nickel oxide powder, ultrasonic dispersion of 20 ~ 100min, adding 5 20mL water, 400 ~ 600 rpm by adding 0.5 ~ 1g of boron Nah, continue stirring for 4 ~ 8min, precipitation separation, a core-shell type nickel oxide / nickel catalyst. As the nickel oxide precursor preparation of nickel and nano particles as a carrier to support the nucleation and growth of the active function, control of nanoparticles surfactants as templates for the growth of function, reducing agent is added to a mixture containing template support dual function micro reaction environment, reduction in the surface part, prepared the kernel for the surface of the nickel oxide is core-shell type catalyst of nickel, and nickel oxide / nickel have synergistic effect, can better promote the catalytic effect.
【技术实现步骤摘要】
一种核壳型氧化镍/镍光催化剂的制备方法
本专利技术涉及环境污染控制新材料的开发，尤其涉及一种核壳型氧化镍/镍光催化剂的制备方法。
技术介绍
在生活污水、食品加工和造纸等工业废水中，含有碳水化合物、蛋白质、油脂、木质素等有机物质。这些物质以悬浮或溶解状态存在于污水中，可通过微生物的生物化学作用而分解。在其分解过程中需要消耗氧气，因而被称为耗氧污染物。这种污染物可造成水中溶解氧减少，影响鱼类和其他水生生物的生长。水中溶解氧耗尽后，有机物进行厌氧分解，产生硫化氢、氨和硫醇等难闻气味，使水质恶化。随着生产的发展，来自工农业生产中产生的毒害有机污染物严重威胁着环境和人类的健康，寻求一种新型高效的环境治理技术具有重要的意义。光催化技术因其节能、高效、污染物降解彻底、无二次污染优点，目前已成为一种具有重要应用前景的新兴环境治理技术。近年来，新型高效的可见光光催化剂的研制成为光催化技术中的一个重要研究内容。过渡金属氧化物大多具有优良的电学和光学特性，也具有优异的催化性能。纳米氧化镍是一种重要的功能材料，由于尺寸与形貌的独特性，其在涂饰、催化、电容电极、光吸收、气敏传感等工业领域中...
【技术保护点】
一种核壳型氧化镍/镍光催化剂的制备方法，其特征是依次包括如下步骤：将1～4g十六烷基三甲基溴化铵溶解到20mL甲苯中，加入4～5g过80～100目筛的氧化镍粉末，超声分散20～100min，加入5～20mL水，在400～600转/分钟的转速下加入0.5～1g硼氢化钠，继续搅拌4～8min，沉淀分离，得到一种核壳型氧化镍/镍光催化剂。
【技术特征摘要】
1.一种核壳型氧化镍/镍光催化剂的制备方法，其特征是依次包括如下步骤：将1～4g十六烷基三甲基溴化铵溶解到20mL甲苯中，加入4～5g过80～100目筛的氧化镍粉末，超...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。