铁酸盐包覆海泡石复合催化剂及其制备方法和应用技术
Ferrite coated Sepiolite Composite Catalyst and preparation method and application thereof
The invention relates to a ferrite coated sepiolite composite catalyst, a preparation method and an application thereof. The technical proposal is that the ferrite is mixed with a proper amount of sepiolite and transferred to the polytetrafluoroethylene reaction tank to be closed. In the microwave digestion apparatus, under microwave hydrothermal pressure 1.5MPa, the microwave hydrothermal reaction 30min, the precipitate was washed to the neutral with super pure water, filtered and dried, and the target product was obtained. As a new method for treating dye wastewater, the present invention has the advantages of high degradation efficiency, quick degradation rate, low cost and no two pollution.
【技术实现步骤摘要】
铁酸盐包覆海泡石复合催化剂及其制备方法和应用
本专利技术属于催化降解领域，具体地涉及微波水热法制备的铁酸盐包覆海泡石复合催化剂及其在微波催化降解水中有机污染物中的应用。
技术介绍
目前，大量的水被用于清洗和染色工艺。与此同时，现代工业活动也给全球的土壤和水造成了广泛的危险污染。其中一类最麻烦的污染物是持久性有机污染物(POPs)，如染料，洗涤剂和农药。由于其水溶性和化学稳定性，这些有色化合物在环境中的存在会导致相当多的污染和严重的健康风险问题。有机染料在纺织、造纸、颜料、食品、化妆品、药品制造等行业中的广泛使用和胡乱处理导致严重的环境危害。染料排放行业主要引起水的污染和对公共环境卫生的健康问题，因为有些染料及其代谢产物有毒，致癌，致畸和致突变。因此，从废水中去除染料具有重要意义。由于传统的污水处理方法不能有效消除这些污染物，所以研究针对染料废水的强有力净化方法，已经受到越来越多的关注。过去的几十年中，纺织印染废水的处理具有颜色深，生物降解性低和毒性高等特点一直是环境保护的主要问题。罗丹明B(RhodamineB)是一种含氮染料，自身通过还原厌氧降解可能会产生潜在的...
【技术保护点】
铁酸盐包覆海泡石复合催化剂，其特征在于，由铁酸盐和海泡石制得，所述的铁酸盐为铁酸锰、铁酸锰镍或铁酸镍。
【技术特征摘要】
1.铁酸盐包覆海泡石复合催化剂，其特征在于，由铁酸盐和海泡石制得，所述的铁酸盐为铁酸锰、铁酸锰镍或铁酸镍。2.根据权利要求1所述的铁酸盐包覆海泡石复合催化剂，其特征在于，铁酸盐与海泡石的质量比为1:1-1.5。3.权利要求1或2所述的铁酸盐包覆海泡石复合催化剂的制备方法，其特征在于，方法如下：将铁酸盐与海泡石混合后，转移到聚四氟乙烯反应罐中，密闭，在微波消解仪中，于水热压力1.5MPa下，微波水热反应30min，过滤，沉淀物用超纯水洗至中性，过滤，干燥，得目标产物。4.根据权利要求3所述的制备方法，其特征在于，所述的铁酸盐为铁酸锰，制备方法包括如下步骤：将硝酸铁与硝酸锰混合，溶于超纯水中，调节pH至12.0，得铁酸锰；按摩尔比，Fe3+:Mn2+＝2:1。5.根据权利要求3所述的制备方法，其特征在于，所述的铁酸盐为铁酸锰镍，制备方法包括如...
【专利技术属性】
技术研发人员：张朝红，富璐，刘逸伦，纪剑峰，孙意忱，郜炜，宋有涛，王君，
申请(专利权)人：辽宁大学，
类型：发明
国别省市：辽宁,21