模板法合成具有多孔结构铁酸镍可见光催化剂的方法技术
Method for synthesizing nickel ferrite visible light catalyst with porous structure by template method
The invention discloses a template synthesis method with porous structure of nickel ferrite photocatalyst, which comprises the following steps: using the molar concentration is 1 ~ 4mol/L alkaline solution treatment of cotton fiber is 1 ~ 8h, and then in the 60 to 120 DEG C drying; soak cotton fiber treated in iron nitrate, nickel nitrate with the formation of citric acid sol in 3 ~ 8h, and then in the 60 to 120 DEG C to dry gel; the gel in the temperature programmed furnace to 1 to 5 DEG /min heating rate of heating to 400 to 800 DEG C calcined 3h, nickel ferrite with furnace cooling to room temperature was prepared with porous structure. The invention uses cotton fiber as a template to synthesize NiFe
【技术实现步骤摘要】
模板法合成具有多孔结构铁酸镍可见光催化剂的方法
本专利技术属于铁酸镍可见光催化剂的合成
，具体涉及一种模板法合成具有多孔结构铁酸镍可见光催化剂的方法。
技术介绍
水污染问题一直影响着人们的生活，相对于传统的废水处理，光催化降解污染物具有速度快、无选择性、反应条件温和、投资少、能耗低和应用范围广等优点。光催化剂是这项技术的核心，TiO2半导体光催化剂得到广泛使用，是由于其催化活性高，无毒，廉价，稳定性好，但TiO2仅能利用太阳光中紫外光部分（波长范围是400nm以下），太阳光利用率低，并且存在催化剂难以回收的难题，因此开发具有磁性的且能够高效利用太阳光的催化剂具有重要的研究意义。近年来，在光催化降解污染物领域，尖晶石铁酸镍（NiFe2O4）的研究开发得到人们的关注，环境友好，低价易得，具有较窄的带隙能，此外其磁性有益于光催化剂的回收，并且具有化学稳定性。NiFe2O4具有可见光光催化活性。但是现有的研发中，NiFe2O4大部分作为电极材料或电导材料；NiFe2O4也可以在H2O2、臭氧的辅助下处理污染物，而直接用于光催化降解污染物的比较少。NiFe2O4的带隙...
【技术保护点】
模板法合成具有多孔结构铁酸镍可见光催化剂的方法，其特征在于具体步骤为：（1）用摩尔浓度为1～4mol/L的碱溶液处理棉纤维1～8h，然后于60～120℃干燥；（2）将处理过的棉纤维浸泡在硝酸铁、硝酸镍与柠檬酸形成的溶胶中3～8h，然后于60～120℃干燥至凝胶；（3）将凝胶在程序升温炉中以1～5℃/min的升温速率升温至400～800℃煅烧3h，随炉冷却至室温制得具有多孔结构的铁酸镍。
【技术特征摘要】
1.模板法合成具有多孔结构铁酸镍可见光催化剂的方法，其特征在于具体步骤为：（1）用摩尔浓度为1～4mol/L的碱溶液处理棉纤维1～8h，然后于60～120℃干燥；（2）将处理过的棉纤维浸泡在硝酸铁、硝酸镍与柠檬酸形成的溶胶中3～8h，然后于60～120℃干燥至凝胶；（3）将凝胶在程序升温炉中以1～5℃/min的升温速率升温至400～800℃煅烧3h，随炉冷却至室温制得具有多孔结构的铁酸镍。2.根据权利要求1所述的模板法合成具有多孔结构铁酸镍可见光催化剂的方法，其特征在于：所述的碱溶液为氢氧化钠溶液。3.根据权利要求1...
【专利技术属性】
技术研发人员：赵晓华，徐莎，娄向东，苏帅，魏崇，王晓兵，李彩珠，
申请(专利权)人：河南师范大学，
类型：发明
国别省市：河南,41