The heat treatment process of a small hoist is characterized by the combination of ferritic chemical heat treatment and austenitic heat treatment. The low temperature chemical heat sulfonitriding processing; and above the critical temperature, high temperature chemical heat carbonitriding treatment; at the same time above the critical temperature, high temperature chemical heat treatment of boronizing; then execute the austenitic nitriding; finally in the implementation and. The invention provides a heat treatment process of a small lifting hoist, which has the advantages of corrosion resistance, wear resistance, long service life, low noise, low cost of use and maintenance, and safety and reliability.
【技术实现步骤摘要】
小型起重葫芦的热处理工艺
本专利技术涉及一种小型起重设备的热处理工艺领域,具体地说是涉及小型起重葫芦的热处理工艺。
技术介绍
本专利技术涉及小型起重葫芦的热处理工艺。现有的小型电动葫芦是由电机、减速器、运行机构、制动器、控制开关、卷筒组成,大部分部件均由金属制成,在使用过程中存在表面腐蚀,生锈的现象,随着使用时间的延长,在金属表面会形成裂纹,裂纹逐步扩展会出现小块金属剥落,造成金属表面的凹凸不平,引起振动和噪声,甚至造成丧失传动能力。同时使用过程会产生磨损,不断的磨损使得金属表面出现划痕,在传动过程中发出噪音,缩短了起重葫芦的使用寿命,增加了施工成本,降低了施工的安全性。
技术实现思路
鉴于现有技术存在的缺陷,本专利技术的目的是弥补现在小型起重葫芦的不足之处,提供一种耐腐蚀,耐磨损,使用寿命长,噪音小,使用和维修成本低,安全可靠的小型起重葫芦的热处理工艺。为实现上述目的,本专利技术所采用的技术解决方案是:小型起重葫芦的热处理工艺是采用铁素体化学热处理和奥氏体热处理相结合的方法。先进行硫氮共渗的低温化学热处理;再在临界温度以上,进行碳氮共渗的高温化学热处理;同时在临界温度以上,进行渗硼的高温化学热处理;再施行奥氏体渗氮;最后在施行调质。具体实施方式(1)将氨气经过净化,通过螺旋管道加热至550℃±50℃,氨气经加热析出氮离子,在混合器中加入硫代硫酸钠,并使温度保持在700℃±50℃之内,并施加0.2±0.05Pa大气压力,硫氮离子经旋流管道形成涡流慢速地充满待处理的部件四周,经过2小时后,降温,在温度降至400℃±50℃时,停止氨气通入,继续降温至部件冷却。(2 ...
【技术保护点】
小型起重葫芦的热处理工艺,其特征在于,采用铁素体化学热处理和奥氏体热处理相结合的方法;先进行硫氮共渗的低温化学热处理;再在临界温度以上,进行碳氮共渗的高温化学热处理;同时在临界温度以上,进行渗硼的高温化学热处理;再施行奥氏体渗氮;最后在施行调质。
【技术特征摘要】
1.小型起重葫芦的热处理工艺,其特征在于,采用铁素体化学热处理和奥氏体热处理相结合的方法;先进行硫氮共渗的低温化学热处理;再在临界温度以上,进行碳氮共渗的高温化学热处理;同时在临界温度以上,进行渗硼的高温化学热处理;再施行奥氏体渗氮;最后在施行调质。2.根据权利要求1所述的小型起重葫芦的热处理工艺,其特征在于,将氨气经过净化,通过螺旋管道加热至550℃±50℃,氨气经加热析出氮离子,在混合器中加入硫代硫酸钠,并使温度保持在700℃±50℃之内,并施加0.2±0.05Pa大气压力,硫氮离子经旋流管道形成涡流慢...
【专利技术属性】
技术研发人员:赵振荣,
申请(专利权)人:青岛三同德金属制品有限公司,
类型:发明
国别省市:山东,37