一种锂离子二次电池正极片中活性物质和铝片的分离回收方法技术

本发明专利技术提供一种锂离子二次电池正极片中活性物质和铝片的分离回收方法。本发明专利技术是通过针对不同活性物质的二次电池正极片进行特定温度的热处理来达到活性物质与铝片的有效分离。该方法工艺简单、成本低廉，可以使正极片上活性物质与纯铝片有效分离，并且活性物质保持原有性质，铝片不熔融粉化、不氧化。

Separation and recovery method of active substance and aluminium sheet in positive plate of lithium ion secondary battery two

The present invention provides a separation and recovery method for active material and aluminum sheet in positive plate of lithium ion secondary battery two. The present invention achieves effective separation between active material and aluminum sheet by thermal treatment of specific temperature of two cell positive plate for different active material. The method has the advantages of simple process and low cost. The active material on the positive plate can be effectively separated from the pure aluminum sheet, and the active substance remains the original nature, and the aluminum sheet is not melted, pulverized and non oxidized.

【技术实现步骤摘要】
一种锂离子二次电池正极片中活性物质和铝片的分离回收方法
本专利技术属于锂离子电池
，涉及一种锂离子二次电池正极片的分离回收方法，更具体的讲涉及锂离子二次电池正极片中活性物质和铝片的分离回收利用方法。
技术介绍
在锂离子电池材料检测和电池制作过程中，会产生许多正极片边角料，正极片边角料由锂电正极材料及铝片组成。由于镍、钴、锰等资源贫乏，金属铝生产耗能高，所以正极片回收有很大价值。在正极片回收领域，目前很多都是采用酸溶解后分离提纯的方法，提纯的镍、钴、锰盐都含有铝杂质，因为铝为絮状沉淀，沉淀颗粒度小，但数量多，铝的絮状沉淀很难过滤除去，如果用这类回收后的镍、钴、锰盐合成正极材料前驱体，絮状氢氧化铝是晶种，给前驱体粒度控制带来很大的麻烦，而且工艺锂无法回收。并且，此类方法投资非常巨大会产生大量的废水，污染环境。因此，需要一种工序简单、成本低廉的方法来分离回收正极片中活性物质和铝片。
技术实现思路
本专利技术公开了一种锂离子二次电池正极片中活性物质和铝片的分离回收方法，该方法工艺简单、成本低廉，可以使正极片上活性物质与纯铝片有效分离，并且活性物质保持原有性质，铝片不熔融粉化、不氧化。本专利本文档来自技高网...

【技术保护点】
一种锂离子二次电池正极片中活性物质和铝片的分离回收方法，包括如下步骤：（1）将正极片于350~450℃下热处理3~5h；（2）取出正极片，自然降至室温；（3）物理震动分离正极片上活性物质。

【技术特征摘要】
1.一种锂离子二次电池正极片中活性物质和铝片的分离回收方法，包括如下步骤：（1）将正极片于350~450℃下热处理3~5h；（2）取出正极片，自然降至室温；（3）物理震动分离正极片上活性物质。2.根据权利要求1所述的锂离子二次电池正极片中活性...

【专利技术属性】
技术研发人员：陈卫东，孙国平，刘大亮，
申请(专利权)人：北京当升材料科技股份有限公司，
类型：发明
国别省市：北京,11