The present invention provides a method for removing iron impurity in a lead zinc chloride, which comprises the following steps: (1) each zinc chloride 150 180g, dissolved in 500ml pure water, use Zinc Oxide or hydrochloric acid to adjust PH3 4, stirring 10min, cooling to room temperature, filtered to remove insoluble substances; (2) to the filtrate rapid analysis of pure zinc powder adding 10g, slightly stirring, filtration and separation of precipitate immediately; (3) heating concentrated to the emergence of a large number of liquid crystal, adding 37% hydrochloric acid 20ml, fractional crystallization stirring cooling to room temperature, at 70 - 80 DEG C drying is finished; the method has the advantages of convenient operation, made of copper and lead impurities content in accordance with HG/T2760 2011 is far less than the standard, get to meet the requirements of zinc sulfate products, has broad application prospects.
【技术实现步骤摘要】
一种氯化锌中去除铁铅杂质的方法
本专利技术涉及一种杂质处理工艺，尤其是一种氯化锌中去除铁铅杂质的方法。
技术介绍
氯化锌是无机盐工业的重要产品之一，它应用范围极广。氯化锌易溶于水，是固体盐中溶解度最大的(25℃，333g/100g)，其原因是溶于水形成配酸H[ZnCl2(OH)]。溶于甲醇、乙醇、甘油、丙酮、乙醚，不溶于液氨。潮解性强，能自空气中吸收水分而潮解。具有溶解金属氧化物和纤维素的特性。熔融氯化锌有很好的导电性能。灼热时有浓厚的白烟生成。氯化锌有腐蚀性，有毒。试剂级氯化锌的制备以往使用盐酸和氧化锌中和制备，由于铅锌性质相近，产品中铅、铁杂质往往不易达到(铅≤0.002％、铁≤0.0005％)的要求，故需要采取高效的去除方法。因此，寻找一种方便有效的去除氯化锌中铁铅杂质的方法具有非常重要的生产实践意义。
技术实现思路
本专利技术所要解决的技术问题在于提供一种氯化锌中去除铁铅杂质的方法。为解决上述技术问题，本专利技术的技术方案是：一种氯化锌中去除铁铅杂质的方法，具体步骤为：(1)每氯化锌150－180g，溶于500ml纯水中，使用氧化锌或盐酸调节PH3－4，搅拌1...
【技术保护点】
一种氯化锌中去除铁铅杂质的方法，其特征在于：具体步骤为：(1)每氯化锌150－180g，溶于500ml纯水中，使用氧化锌或盐酸调节PH3－4，搅拌10min，冷却至室温，过滤除去不溶物；(2)向滤液中快速加入分析纯锌粉10g，稍加搅拌，立即过滤分离沉淀；(3)清液加热浓缩至出现大量晶体，补加37％盐酸20ml，搅拌冷却至室温，分离结晶，在70－80℃干燥，即得成品。
【技术特征摘要】
1.一种氯化锌中去除铁铅杂质的方法，其特征在于：具体步骤为：(1)每氯化锌150－180g，溶于500ml纯水中，使用氧化锌或盐酸调节PH3－4，搅拌10min，冷却至室温，过滤除去不溶物；(2)向滤液中快速加入分析纯锌粉10g，稍加搅拌，立即过滤分离...