本发明专利技术涉及一种汽车钣金件制备方法，所述工艺流程涉及汽车左右导风罩钣金件的制造工序和流程，包括以下制造工序：工序1，剪板机下料；工序2，模具定尺料切冲；工序3，模具成型；工序4，模具折弯；工序5，模具分离冲孔；工序6，对接电阻焊；工序7，酸洗.磷化；工序8，静电喷涂；工序9，装车入库。本发明专利技术提高了材料和设备利用率；极大提高了工作效率和产品合格率。对原料参数进行了设计，对加工过程中的设备进行了设计，对加工工序和工艺进行了设计，达到了良好的效果。

Method for preparing automobile sheet metal parts

The invention relates to a preparation method of automotive sheet metal, the process involves the car around the wind guide cover the manufacturing process of metal parts and processes, including the following: Step 1, manufacturing process of material cutting machine; step 2, mold fixed length punching process; 3, molding process; 4, bending die step 5, mould separation; punching; butt resistance welding; step 6, step 7, step 8. Pickling phosphating; electrostatic spraying process; 9, loading and storage. The invention improves the utilization ratio of materials and equipment, and greatly improves work efficiency and product qualification rate. The raw material parameters are designed, the equipment in the processing process is designed, and the processing steps and processes are designed, and good results are achieved.

【技术实现步骤摘要】
汽车钣金件制备方法
本专利技术属于机械制造领域，具体涉及一种汽车钣金件制备方法。
技术介绍
在汽车左右导风罩钣金件制作过程中，现有技术工艺流程工序不合理，设备利用率低，工作效率低，上下工序衔接不够周密，存在擦除油污和清焊渣等多处多人力操作，生产节拍对实现流水作业不协调，严重影响现代化大生产需求，产品合格率低，严重影响产品质量。
技术实现思路
本专利技术克服了现有技术的不足，提出了一种汽车钣金件制备方法，该流程对汽车左右导风罩钣金件的毛坯尺寸进行了设计，在不影响质量的前提下提高材料利用率；对模具工作参数和设备参数进行对应计算，保证合理使用，避免造成能源浪费；对工作现场的布局进行调整，尽量能流水作业以提高效率；对冲压工序通过技术论证，针对工序的先后顺序和工序的合并等问题进行调整或改进；对焊接工艺工序进行调整，以达到节能降耗目的；对工件加工时产生的油污、锈蚀从根本解决，对边角料进行了处理，达到物尽其用。本专利技术的技术方案为：一种汽车钣金件制备方法，所述工艺流程涉及汽车左右导风罩钣金件的制造工序和流程，包括以下制造工序：工序1，剪板机下料；工序2，模具定尺料切冲；工序3，模具成型；工序4，模具本文档来自技高网...

【技术保护点】
一种汽车钣金件制备方法，所述工艺流程涉及汽车左右导风罩钣金件的制造工序和流程，其特征在于：包括以下制造工序：工序1，下料；工序2，模具定尺料切冲；工序3，模具成型；工序4，模具折弯；工序5，模具分离冲孔；工序6，对接电阻焊；工序7，酸洗,磷化；工序8，静电喷涂；工序9，装车入库。

【技术特征摘要】
1.一种汽车钣金件制备方法，所述工艺流程涉及汽车左右导风罩钣金件的制造工序和流程，其特征在于：包括以下制造工序：工序1，下料；工序2，模具定尺料切冲；工序3，模具成型；工序4，模具折弯；工序5，模具分离冲孔；工序...

【专利技术属性】
技术研发人员：不公告发明人，
申请(专利权)人：青岛纵横农业科技有限公司，
类型：发明
国别省市：山东,37