The invention relates to the technical field of processing and processing of resin parts, in particular to a cleaning method for resin parts. The steps are as follows: 1), the resin parts with deionized water spray cleaning; 2), wipe the surface with ether, dried for use; 3), used in containers of ultrasonic cleaning, resin parts cleaning agent in the container, the container temperature control for 20 40 DEG C; 4), after the removal of ultrapure water then spray on it, then dried at 50 DEG C. The invention can improve the cleaning performance of the cleaning agent for resin parts by more than 80% by adding a reasonably designed component, in particular by adding acetyl radical. The preparation process parameters are reasonable and the processing cost is low. In addition, the cleaning method of the resin product is relatively simple, and the cleaning efficiency is high.
【技术实现步骤摘要】
树脂制件的清洗方法
本专利技术涉及树脂制件加工处理
,具体是涉及一种树脂制件的清洗方法。
技术介绍
树脂制件在加工过程中,一般要进行清洗。但是,现有的用于树脂制件清洗的清洗剂以及清洗方法,主要存在清洗不彻底,清洗效率低等缺陷。
技术实现思路
本专利技术的目的在于提供一种树脂制件清洗剂及其制备方法、树脂制件的清洗方法,为实现上述目的,本专利技术采用了以下技术方案:一种树脂制件清洗剂,由以下重量份的组分制成:20份水、12.5份十二烷基硫酸钠、10份甘油、10.5份硫酸钾铝、15份碳酸氢钠、17份乙氧基胺和5.5份去乙酰基原藜芦碱。一种树脂制件清洗剂的制备方法,步骤如下:①、将10份水、12.5份十二烷基硫酸钠、10份甘油和10.5份硫酸钾铝加入至反应釜中,于50℃下搅拌1小时;②、将10份水、15份碳酸氢钠、17份乙氧基胺和5.5份去乙酰基原藜芦碱加入至反应釜中,于80℃下搅拌0.5小时;③、自然冷却至常温,然后过滤,去除固形物,得到清洗剂。一种树脂制件的清洗方法,步骤如下:1)、将树脂制件用去离子水喷淋清洗;2)、用乙醚进行表面擦拭,自然晾干待用;3)、置于容器中采用超声波清洗,容器内盛有树脂制件清洗剂,容器内温度控制为20-40℃;4)、取出后再用超纯水对其进行喷淋,接着于50℃下烘干。本专利技术的有益效果表现在:本专利技术通过加入合理设计的组分,特别是加入去乙酰基原藜芦碱,可以提升树脂制件清洗剂的清洗性能约80%以上。这种制备工艺参数设计合理,加工成本低。另外,这种树脂制件的清洗方法比较简单,清洗效率高。具体实施方式以下将结合实施例,对本专利技术进行 ...
【技术保护点】
一种树脂制件的清洗方法,其特征在于:步骤如下:1)、将树脂制件用去离子水喷淋清洗;2)、用乙醚进行表面擦拭,自然晾干待用;3)、置于容器中采用超声波清洗,容器内盛有树脂制件清洗剂,容器内温度控制为20‑40℃;4)、取出后再用超纯水对其进行喷淋,接着于50℃下烘干。
【技术特征摘要】
1.一种树脂制件的清洗方法,其特征在于:步骤如下:1)、将树脂制件用去离子水喷淋清洗;2)、用乙醚进行表面擦拭,自然晾干待用;3)、置...
【专利技术属性】
技术研发人员:姚海明,
申请(专利权)人:芜湖乐普汽车科技有限公司,
类型:发明
国别省市:安徽,34