The invention discloses a low cost and high performance stuffing, which is mainly prepared by mixing the components of the following weight parts: 80~90 parts of sorghum straw powder, 5~10 parts of talcum powder and 5~10 parts of molybdenum disulfide. The sorghum straw carbon powder is a carbon powder obtained by washing, drying, crushing, pressing, block, carbonization and graphitization treatment of the sorghum stalk in sequence. The invention makes full use of Sorghum Planting by-product the sorghum stalk, carbonization and graphitization, artificial graphite materials, graphite powder as a natural alternative to the friction material, friction material can effectively reduce the production cost, expand the channels of sorghum straw, sorghum straw increased economic benefits.
【技术实现步骤摘要】
一种低成本高性能填料
本专利技术涉及一种低成本高性能填料。
技术介绍
高粱，拉丁文名：Sorghumbicolor(L.)Moench禾本科、高粱属一年生草本植物。秆较粗壮，直立，基部节上具支撑根。叶鞘无毛或稍有白粉；叶舌硬膜质，先端圆，边缘有纤毛。[1]性喜温暖，抗旱、耐涝。按性状及用途可分为食用高粱、糖用高粱、帚用高粱等类。中国栽培较广，以东北各地为最多。食用高粱谷粒供食用、酿酒。收割高粱之后，会产生大量的副产物---高粱秆。通常人们处理方式是直接焚烧，这种方式虽然对其进行了一定利用，但是焚烧产生的烟尘大，在一定程度上污染环境。目前，随着工业化的发展，摩擦材料的使用量越来越大，其填料---石墨的使用量也是逐年增加。然而天然石墨的价格还是较高的，而高粱秆中含有大量碳源，如果采用高粱秆制成的碳粉取代石墨添加到摩擦材料中，将极大的降低了摩擦材料的生产成本。
技术实现思路
本专利技术的目的在于提供一种低成本高性能填料。本专利技术充分利用了高粱的副产物---高粱秆，将其进行碳化、石墨化，制成人造石墨材料，作为天然石墨粉的替代品加入到摩擦材料中，有效降低了摩擦材料的生产成本，拓宽高粱秆的利用渠道，提高了高粱秆的经济效益。为了实现上述目的，本专利技术采用了以下技术方案：一种低成本高性能填料，主要由以下重量份数的组分混合配制而成：高粱秆碳粉80～90份、滑石粉5～10份和二硫化钼5～10份。作为本专利技术进一步优选的方案，该低成本高性能填料主要由以下重量份数的组分混合配制而成：高粱秆碳粉85份、滑石粉7份和二硫化钼8份。进一步说明，所述的高粱秆碳粉是将高粱秆依次经清洗烘干...
【技术保护点】
一种低成本高性能填料，其特征在于，主要由以下重量份数的组分混合配制而成：高粱秆碳粉80～90份、滑石粉5～10份和二硫化钼5～10份。
【技术特征摘要】
1.一种低成本高性能填料，其特征在于，主要由以下重量份数的组分混合配制而成：高粱秆碳粉80～90份、滑石粉5～10份和二硫化钼5～10份。2.根据权利要求1所述的低成本高性能填料，其特征在于，主要由以下重量份数的组分混合配制而成：高粱秆碳粉85份、滑石粉7份和二硫化钼8份。3.根据权利要求1或2所述的低成本高性能填料，其特征在于：所述的高粱秆碳粉是将高粱秆依次经清洗烘干、粉碎压制成块、碳化处理、石墨化处理之后获得的碳粉末。4.根据权利要求3所述的低成本高性能填料，其特征在于：所述的碳化处理具体为：将高粱秆块放入贫氧炉进行碳化处理；排潮期从点火至炉温上升到150℃，时间为5小时；然后升温至250℃，打开鼓风机，对炉内鼓...
【专利技术属性】
技术研发人员：卢怡臻，
申请(专利权)人：广西南宁胜祺安科技开发有限公司，
类型：发明
国别省市：广西,45