The present invention provides a water soluble polyester resin, the raw materials are as follows by weight portions: three trihydroxymethylenepropane 15 ~ 18, 25 ~ 30 copies of neopentyl glycol, isophthalic acid two 5 sulfonate 18 - 22, 25 - 30, six adipic acid tetrahydrophthalic two formic acid 5 - 8, ethylene glycol butyl ether 12 ~ 15, 8 ~ 10 sec butanol and two butyl tin oxide from 0.05 to 0.08, two from 8 to 10 monomethylethanolamine. The invention mainly includes the introduction of a non benzene ring two yuan of yogurt group monomer, improve the water solubility, and the backbone of water directly into the functional monomer between two formic acid 5 sulfonate, obtain waterborne polyester resin, the invention also provides the production method and functional additives based on it.
【技术实现步骤摘要】
一种水性聚酯树脂、制备方法及基于其的功能性助剂
本专利技术属于水性涂料功能助剂和制备方法
，涉及一种水性聚酯树脂。
技术介绍
近年来，随着汽车涂装技术的要求越来越高，聚酯树脂涂料因优异的性能在行业内的用量也逐年增加。而目前所使用的聚酯树脂主要还是以溶剂型为主，在倡导低碳环保的今天，水性聚酯以其优异的性能和低VOC排放量势必会成为21世纪环保型涂料发展前研。水性聚酯树脂有以下优点：①优异的硬度与柔韧平衡；②因极性关系，对底材及复合涂层均有极佳的层间附着力，抗石击性好；③高光泽和极佳的丰满度；④良好的耐候、耐水、耐溶剂及耐老化；⑤环境友好，低VOC排放；⑥树脂粒子对机械搅拌、加热和稀释的敏感性小，具有良好的耐水解性和弹性。现有水性漆涂层附着力的不足，尤其在金属表面涂装和装饰，并且其良好的水溶性、稳定性、光泽度高、耐候性性能均不理想。
技术实现思路
本专利技术的目的是提供一种水性聚酯树脂，解决上述技术问题中的一个或者多个。一方面，本专利技术提供一种水性聚酯树脂，由重量份数如下的各原料组成：三羟甲基丙烷15～18份、新戊二醇25～30份、间苯二甲酸-5-磺酸钠18～22...
【技术保护点】
一种水性聚酯树脂，其特征在于，由重量份数如下的各原料组成：三羟甲基丙烷15～18份、新戊二醇25～30份、间苯二甲酸‑5‑磺酸钠18～22份、己二酸25～30份、六氢化邻苯二甲酸5～8份、乙二醇丁醚12～15份、仲丁醇8～10份、二丁基氧化锡0.05～0.08份、二甲基乙醇胺8～10份。
【技术特征摘要】
1.一种水性聚酯树脂，其特征在于，由重量份数如下的各原料组成：三羟甲基丙烷15～18份、新戊二醇25～30份、间苯二甲酸-5-磺酸钠18～22份、己二酸25～30份、六氢化邻苯二甲酸5～8份、乙二醇丁醚12～15份、仲丁醇8～10份、二丁基氧化锡0.05～0.08份、二甲基乙醇胺8～10份。2.一种水性聚酯树脂的制备方法，其特征在于，包括如下步骤；将25～30重量份新戊二醇、15～18重量份三羟甲基丙烷、18～22重量份间苯二甲酸-5-磺酸钠，25～30重量份己二酸和0.05～0.08重量份二丁基氧化锡加入带搅拌器和冷凝管的反应容器中，通氮气，缓慢升温至13...