The invention relates to a process for the preparation of graphene, step as follows: 80 120mg graphene oxide is added to the 250ml flask, add 80 120ml deionized water, ultrasonic treatment to dissolve, adding ammonia to adjust the pH value to 8 9; add 8 15uL80% hydrazine hydrate, oil bath heating to 95 C, under the protection of nitrogen reflux 1 6 hours, until all the black product precipitation; the black precipitate centrifugal analysis, the product with water to neutral, with 3 methanol washing 5 times, drying for. The invention adopts hydrazine hydrate to carry out reduction treatment to the oxidized graphite, and can ensure that the graphite oxide is not re graphitized in the reduction process, and can be sufficiently reduced.
【技术实现步骤摘要】
石墨烯的制备工艺
本专利技术属于高分子材料
，具体涉及一种石墨烯的制备工艺。
技术介绍
化学法在制备石墨烯的过程中，由于强烈的插层和氧化作用，导致片层表面和边缘含有丰富的官能团，片层表面和边缘缺陷较多，以致氧化态的石墨炼逐渐由零带隙的半金属转变为半导体，直至变成绝缘体，影响其在诸多领域中的应用。
技术实现思路
针对以上不足之处，本专利技术旨在提供一种无损的石墨烯制备工艺。一种石墨烯的制备工艺，歩骤如下：将80-120mg氧化石墨烯加入到250ml烧瓶中，加入80-120ml去离子水，超声处理至全部溶解，加入氨水调节pH值至8-9；加入8-15uL80%水合肼，油浴加热至95°C，氮气保护下冷凝回流1-6小时，直至黑色产物全部析出；将黑色沉淀物离心分析，将产物水洗至中性，再以甲醇洗涤3-5次，干燥待用。水合肼是一种无色透明油状液体，以二聚物形式存在，与水和乙醇混溶，不溶于乙醚和氯仿，具有强碱性和吸湿性，还原性极强。反应原理为：肼与羰基缩合生成腙，在碱作用下氮上的质子脱去，双键位移重排，脱去N2，生成的碳负离子从水中夺取质子。本专利技术采用了水合肼对氧化态石墨稀进行还原处理，既可保证氧化石墨烯在还原过程中不发生重新石墨化，又能使其得到充分还原。具体实施方式下面结合具体实施例对本专利技术做进一步详细说明。实施例1一种石墨烯的制备工艺，歩骤如下：将80mg氧化石墨烯加入到250ml烧瓶中，加入100ml去离子水，超声处理至全部溶解，加入氨水调节pH值至8；加入10uL80%水合肼，油浴加热至95°C，氮气保护下冷凝回流3小时，直至黑色产物全部析出；将黑色沉淀物离...
【技术保护点】
一种石墨烯的制备工艺，其特征在于，歩骤如下：将80‑120mg氧化石墨烯加入到250ml烧瓶中，加入80‑120ml去离子水，超声处理至全部溶解，加入氨水调节pH值至8‑9；加入8‑15 uL 80%水合肼，油浴加热至95°C，氮气保护下冷凝回流1‑6小时，直至黑色产物全部析出；将黑色沉淀物离心分析，将产物水洗至中性，再以甲醇洗涤3‑5次，干燥待用。
【技术特征摘要】
1.一种石墨烯的制备工艺，其特征在于，歩骤如下：将80-120mg氧化石墨烯加入到250ml烧瓶中，加入80-120ml去离子水，超声处理至全部溶解，加入氨水调节pH值至8-9...
【专利技术属性】
技术研发人员：孙国志，
申请(专利权)人：青岛智信生物科技有限公司，
类型：发明
国别省市：山东,37