The invention discloses a processing method of biochar, according to weight ratio, the rice straw, rape straw, bamboo, wood and grass; rice straw, rape straw, sawdust and weeds were crushed and broken; the bamboo segmented into strips; stirring into hydrochloric acid solution, mixed evenly; the mixture is poured into a mold that tie into the mold, the mold is closed in the stove is heated to 700 degrees Celsius 900, 1 hours after cooling into the compressor; pressing, compaction is obtained after biochar. Compared with the prior art, the invention adopts a variety of waste straw production, through the compression of the biochar compaction, improve the combustion time of biochar, reduce the biological carbon storage volume, easy to use, has the value of application.
【技术实现步骤摘要】
一种生物炭加工方法
本专利技术涉及一种生物炭,尤其涉及一种生物炭加工方法。
技术介绍
生物炭是生物有机材料(生物质)在缺氧或绝氧环境中,经高温热裂解后生成的固态产物。既可作为高品质能源、土壤改良剂,也可作为还原剂、肥料缓释载体及二氧化碳封存剂等,已广泛应用于固碳减排、水源净化、重金属吸附和土壤改良等,可在一定程度上为气候变化、环境污染和土壤功能退化等全球关切的热点问题提供解决方案。现有技术中,生物炭的燃烧时效短,燃烧效率低,因此,存在改进空间。
技术实现思路
本专利技术的目的就在于为了解决上述问题而提供一种生物炭加工方法。本专利技术通过以下技术方案来实现上述目的:本专利技术包括以下步骤:(1)按重量比,取水稻秸秆20%、油菜秸秆10%、竹节40%、木屑20%和杂草10%;(2)将水稻秸秆、油菜秸秆、木屑和杂草均粉碎;(3)将竹节分段并破碎成条状;(4)将步骤(2)的物质中加入盐酸溶液进行搅拌,混合均匀;(5)将步骤(4)的混合物倒入模具中,扎入模具中,将模具位于炉具中密闭加温至700-900摄氏度,保温1小时;(6)将步骤(5)的产物冷却后放入压缩机中压制,压实后即得生物炭。本专利技术的有益效果在于:本专利技术是一种生物炭加工方法,与现有技术相比,本专利技术采用多种废弃秸秆制作,通过压缩将生物炭压实,提高生物炭的燃烧时效,减少生物炭的储存体积,使用方便,具有推广应用的价值。具体实施方式下面对本专利技术作进一步说明:本专利技术包括以下步骤:(1)按重量比,取水稻秸秆20%、油菜秸秆10%、竹节40%、木屑20%和杂草10%;(2)将水稻秸秆、油菜秸秆、木屑和杂草 ...
【技术保护点】
一种生物炭加工方法,其特征在于,包括以下步骤:(1)按重量比,取水稻秸秆20%、油菜秸秆10%、竹节40%、木屑20%和杂草10%;(2)将水稻秸秆、油菜秸秆、木屑和杂草均粉碎;(3)将竹节分段并破碎成条状;(4)将步骤(2)的物质中加入盐酸溶液进行搅拌,混合均匀;(5)将步骤(4)的混合物倒入模具中,扎入模具中,将模具位于炉具中密闭加温至700‑900摄氏度,保温1小时;(6)将步骤(5)的产物冷却后放入压缩机中压制,压实后即得生物炭。
【技术特征摘要】
1.一种生物炭加工方法,其特征在于,包括以下步骤:(1)按重量比,取水稻秸秆20%、油菜秸秆10%、竹节40%、木屑20%和杂草10%;(2)将水稻秸秆、油菜秸秆、木屑和杂草均粉碎;(3)将竹节分段并破碎成条状;(4)将步...