The invention relates to a preparation process of new steel head, which is characterized in that the metal filter layer thickness is less than or equal to 10mm, after the hot metal mixing screening, screening for 30min, after screening the temperature drop is less than or equal to 30 DEG C; the screening of the molten iron after adding stainless steel powder in the furnace smelting, smelting temperature > 1370; C, smelting after tapping, argon blowing argon for treatment; 5min, 700-900NL/min flow, the temperature of molten steel > 1650 DEG C; the invention has the advantages that the design is scientific and convenient preparation, no pollution, economical and convenient generalization and reliable safety.
【技术实现步骤摘要】
一种新型钢材料封头的制作工艺
本专利技术主要涉及一种封头,尤其涉及一种新型钢材料封头的制作工艺。
技术介绍
目前，近年来，国产对封头的使用特别广泛，容器钢板发展的推动作用。与旧版的压力容器用钢板相比，提高了各品牌号封头指标，封头容器用板的质量与性能都有一定的提高，对压封头用钢的要求也严格了。它规定了碳素钢和低合金钢冲击功(KV2)最小不低于20J。焊接结构用碳素钢低合金高强度钢和低合金低温钢钢板，器断后伸长率(A)最小不低于17％。随着国内工业水平的提高，国内容器用板的质量性能的提高，缩小了与发达国家的差距。对于碳素钢冷成形封头是否应该热处理的问题。
技术实现思路
本专利技术的目的是克服上述现有工艺存在的不足，而提供一种新型钢材料封头的制作工艺。本专利技术的技术方案是：一种新型钢材料封头的制作工艺，其特征在于：将铁水进行过滤层厚度≤10mm，之后铁水进行搅拌进行筛选处理，筛选时间为30min，筛选后温降≤30℃；将筛选后的铁水内加入不锈钢粉在炉中冶炼，冶炼温度>1370℃，冶炼之后进行出钢，进行吹氩处理；吹氩5min，流量700-900NL/min，钢液温度>1650℃；加入精炼脱氧剂，加热15-20min，30—50min后进行加热10-15min，再次加入镁粉；在80Pa以下保压20min，之后抽真空，进行浇铸：浇铸时上钢温度>1700℃；倒入封头胎膜内，使封头成形，成形后冷却处理清洗包装成品封头。本专利技术的优点是：设计科学、制备方便、安全可靠无污染、经济适用、便于推广。具体实施例下面结合一个实施例，对本专利技术提供种新型钢材料封头的制...
【技术保护点】
一种新型钢材料封头的制作工艺，其特征在于：将铁水进行过滤层厚度≤10mm，之后铁水进行搅拌进行筛选处理，筛选时间为30min，筛选后温降≤30℃；将筛选后的铁水内加入不锈钢粉在炉中冶炼，冶炼温度>1370℃，冶炼之后进行出钢，进行吹氩处理；吹氩5min，流量700‑900NL/min，钢液温度>1650℃；加入精炼脱氧剂，加热15‑20min，30—50min后进行加热10‑15min，再次加入镁粉；在80Pa以下保压20min，之后抽真空，进行浇铸：浇铸时上钢温度>1700℃；倒入封头胎膜内，使封头成形，成形后冷却处理清洗包装成品。
【技术特征摘要】
1.一种新型钢材料封头的制作工艺，其特征在于：将铁水进行过滤层厚度≤10mm，之后铁水进行搅拌进行筛选处理，筛选时间为30min，筛选后温降≤30℃；将筛选后的铁水内加入不锈钢粉在炉中冶炼，冶炼温度>1370℃，冶炼之后进行出钢，进行吹氩处理；吹氩5min，流量700-90...
【专利技术属性】
技术研发人员：季振宽，
申请(专利权)人：青岛旭升封头有限公司，
类型：发明
国别省市：山东,37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。