The invention discloses a cotton coating dyeing process, the dyeing process of a cotton coating, characterized by comprising the following steps: 1) the socks with atmospheric dielectric barrier discharge plasma pretreatment, control and processing power of 2500-3500W, the processing time for 8-12 minutes; 2) of cotton coating dyeing processing, the coating dyeing processing includes coating, adhesive, dyeing dip continued dehydration, drying and baking, the coating phase dip coating selection particle size of 50-150 nm, the adhesive adhesive continued dyeing acrylic adhesive. The method has the advantages of high efficiency, low cost, low cost, environmental friendliness, good dyeing effect and firm color.
【技术实现步骤摘要】
本专利技术涉及纺织品处理领域，尤其涉及一种棉袜的涂料染色工艺。
技术介绍
传统的涂料染色工艺，存在染色织物手感差、容易掉色的问题，而且环境污染较大，在节能减排环境友好的向导下，人们需要找到更好的解决办法。
技术实现思路
本专利技术所要解决的技术问题是提供一种能常压下完成、清洁高效、染色效果好的棉袜的涂料染色工艺。本专利技术是通过以下技术方案来实现的：一种棉袜的涂料染色工艺，其特征在于，包括如下步骤：1）将棉袜用常压介质阻挡放电等离子体进行预处理，控制处理功率为2500-3500W,处理时间为8-12分钟；2）对棉袜进行涂料染色处理，所述涂料染色处理包括涂料浸染、粘合剂续染、脱水、烘干和焙烘，所述涂料浸染阶段涂料选用粒径为50-150纳米，粘合剂续染阶段粘合剂选用聚丙烯酸类粘合剂。本专利技术的有益效果是：该涂料染色方法，常压处理，快速清洁高效，处理成本低，环境友好，且染色效果好、色牢，值得推广。具体实施方式一种棉袜的涂料染色工艺，其特征在于，包括如下步骤：1）将棉袜用常压介质阻挡放电等离子体进行预处理，控制处理功率为2500-3500W,处理时间为8-12分钟；2）对棉袜进行涂料染色处理，所述涂料染色处理包括涂料浸染、粘合剂续染、脱水、烘干和焙烘，所述涂料浸染阶段涂料选用粒径为50-150纳米，粘合剂续染阶段粘合剂选用聚丙烯酸类粘合剂。本专利技术的涂料染色方法，在常压下处理，快速清洁高效，处理成本低，环境友好，且染色效果好、色牢，值得推广。以上所述，仅为本专利技术的具体实施方式，但本专利技术的保护范围并不局限于此，任何不经过创造性劳动想到的变化或替换，都应涵盖...
【技术保护点】
一种棉袜的涂料染色工艺，其特征在于，包括如下步骤：1）将棉袜用常压介质阻挡放电等离子体进行预处理，控制处理功率为2500‑3500W,处理时间为8‑12分钟；2）对棉袜进行涂料染色处理，所述涂料染色处理包括涂料浸染、粘合剂续染、脱水、烘干和焙烘，所述涂料浸染阶段涂料选用粒径为50‑150纳米，粘合剂续染阶段粘合剂选用聚丙烯酸类粘合剂。
【技术特征摘要】
1.一种棉袜的涂料染色工艺，其特征在于，包括如下步骤：1）将棉袜用常压介质阻挡放电等离子体进行预处理，控制处理功率为2500-3500W,处理时间为8-12分钟；2）对棉...
【专利技术属性】
技术研发人员：王卫平，
申请(专利权)人：江阴市超宇针织有限公司，
类型：发明
国别省市：江苏;32