Wide stainless steel shell grow hollow profile and its manufacturing process belongs to the field of production technology for large passenger rail thin parts, the section is composed of a decorative outer plate, located in the connection of a corrugated plate, interlayer board sequentially by laser welding; three layers of material are made of stainless steel plate, decorative plate plate thickness is 1.5mm 2.5mm, wire drawing processing or DF surface treatment, in the plate thickness is 1mm 1.5mm, section structure of decorative outer and inner plates are flat, or by roll forming sections with rib pressing, or edge profile bending, bending plate or corrugated plate; the plate thickness is 0.5mm 0.8mm, single section corrugated corrugated plate is trapezoid or rectangular, corrugated plate section is section or section structure. The stainless steel hollow section material of the invention eliminates the complicated process of small parts assembly, has the advantages of simple process and high efficiency, and has the advantages of good rigidity, no deformation, etc..
【技术实现步骤摘要】
本专利技术属于轨道客车用宽大薄部件生产
,具体涉及一种宽幅长大薄壳不锈钢中空型材及其制造工艺,适用于宽度为300mm-1250mm、长度为10000mm-30000mm、厚度为20mm-70mm的宽大薄部件的生产。
技术介绍
铝合金宽幅中空型材采用体积热挤压工艺技术制造,可以挤出宽幅长大件,广泛用于轨道车辆中。宽幅长大型材的使用可以大大减少零件数量,简化工艺。但是铝合金材料的耐蚀性、强度、防火能力等使用性能方面远远不如不锈钢材料。挤压工艺的局限性导致铝合金宽幅长大挤压型材不能得到薄壳高强度型材。不锈钢材料不能通过挤压方法得到宽幅中空型材,所以以往不锈钢材料宽幅长大结构件只能设计成板梁组焊结构,通过预先制造的几十个甚至几百个零件组对、焊接得到,不能实现不锈钢宽幅长大零件的连续化和自动化生产,工艺复杂、效率低,质量不易保证。
技术实现思路
为了解决现有采用不锈钢板梁结构和制造工艺中存在的工艺复杂、周期长、效率低、质量差等技术问题,本专利技术提供一种宽幅长大薄壳不锈钢中空型材及其制造工艺。本专利技术解决技术问题所采取的技术方案如下:宽幅长大薄壳不锈钢中空型材,其由装饰性外板、位于中间夹层的波纹板、内板顺次通过激光搭接焊连接构成;所述装饰性外板的材料为不锈钢板,板厚为1.5mm-2.5mm,表面进行拉丝处理或DF处理,装饰性外板的断面结构是平板,或者是通过辊弯成型的带有压筋的型材,或者是边缘压弯的型材,或者是弯板;所述波纹板的材料为不锈钢板,板厚为0.5mm-0.8mm,波纹板的单个波纹断面为梯形或矩形,波纹板的断面是均断面或者变断面结构;所述内板的材料为不锈 ...
【技术保护点】
宽幅长大薄壳不锈钢中空型材,其特征在于,该型材由装饰性外板、位于中间夹层的波纹板、内板顺次通过激光搭接焊连接构成;所述装饰性外板的材料为不锈钢板,板厚为1.5mm‑2.5mm,表面进行拉丝处理或DF处理,装饰性外板的断面结构是平板,或者是通过辊弯成型的带有压筋的型材,或者是边缘压弯的型材,或者是弯板;所述波纹板的材料为不锈钢板,板厚为0.5mm‑0.8mm,波纹板的单个波纹断面为梯形或矩形,波纹板的断面是均断面或者变断面结构;所述内板的材料为不锈钢板,板厚为1mm‑1.5mm,内板的断面结构是平板,或者是通过辊弯成型的带有压筋的型材,或者是边缘压弯的型材,或者是弯板。
【技术特征摘要】
1.宽幅长大薄壳不锈钢中空型材,其特征在于,该型材由装饰性外板、位于中间夹层的波纹板、内板顺次通过激光搭接焊连接构成;所述装饰性外板的材料为不锈钢板,板厚为1.5mm-2.5mm,表面进行拉丝处理或DF处理,装饰性外板的断面结构是平板,或者是通过辊弯成型的带有压筋的型材,或者是边缘压弯的型材,或者是弯板;所述波纹板的材料为不锈钢板,板厚为0.5mm-0.8mm,波纹板的单个波纹断面为梯形或矩形,波纹板的断面是均断面或者变断面结构;所述内板的材料为不锈钢板,板厚为1mm-1.5mm,内板的断面结构是平板,或者是通过辊弯成型的带有压筋的型材,或者是边缘压弯的型材,或者是弯板。2.如权利要求...