The present invention relates to the technical field of surface engineering, which relates to a preparation method of non parts and the application of the surface protection material and method for spraying comprises the following raw materials by weight percent: 60 meter lead dioxide 70%, 3 gum 5%, water margin; parts coating surface protection material preparation method, which comprises the following steps: lead white powder, gum and water mixing evenly, non coating surface protection material component. The invention of the parts non coating surface protection material has the advantages of low cost, easy removal, green environmental protection, will not cause secondary pollution to the advantages of the two thermal spraying, and the preparation method is simple and convenient application, can be widely used in mechanical parts thermal spraying spraying non surface protection.
【技术实现步骤摘要】
本专利技术涉及表面工程
,涉及一种零件非喷涂面保护材料及其制备方法和应用。
技术介绍
机械零部件为了提高耐磨、抗腐蚀、微动磨损等功能,需要在局部区域采用热喷涂的方法喷涂一层涂层,这样一来没有喷涂的区域(即非喷涂面)就要采用人工方法进行保护。目前通常采用的方法是贴专用保护胶带或采用专用工装,这些方法成本高、保护和去除时间长,这主要是因为保护胶带只能使用一次,不能重复使用,若采用专用工装则设计和制造成本高,对于某些复杂型面的保护工装设计难度大。随着热喷涂的广泛应用,急需一种低成本、可以快速对非喷涂面进行保护且保护层容易去除的新方法。
技术实现思路
本专利技术的目的在于克服现有技术的不足,提供一种零件非喷涂面保护材料及其制备方法和应用,采用涂料保护需要进行热喷涂的零件的非喷涂面,低成本,易去除,不会对热喷涂涂层造成二次污染。本专利技术的目的是通过以下技术方案来实现的:一种零件非喷涂面保护材料,由以下原料以质量百分比计组成:铅白粉60-70%,树胶3-5%,水余量。上述零件非喷涂面保护材料的制备方法,包括以下步骤:将铅白粉、树胶和水搅拌混合均匀,得到零件非喷涂面保护材料。进一步地,所述搅拌混合时间为5-10min。上述零件非喷涂面保护材料的应用,由上述的方法制备零件非喷涂面保护材料,放置3-5min,然后涂在用于热喷涂的零件非喷涂面。上述零件非喷涂面保护材料的去除方法,用水冲洗零件非喷涂面保护材料,现实快速去除。本专利技术一种零件非喷涂面保护材料及其制备方法和应用的有益效果是:本专利技术的零件非喷涂面保护材料具有低成本,易去除,绿色环保,不会对热喷涂涂层造成二 ...
【技术保护点】
一种零件非喷涂面保护材料,其特征在于,由以下原料以质量百分比计组成:铅白粉 60‑70%,树胶 3‑5%,水 余量。
【技术特征摘要】
1.一种零件非喷涂面保护材料,其特征在于,由以下原料以质量百分比计组成:铅白粉60-70%,树胶3-5%,水余量。2.一种如权利要求1所述零件非喷涂面保护材料的制备方法,其特征在于,包括以下步骤:将铅白粉、树胶和水搅拌混合均匀,得到零件非喷涂面保护材料。3.根据权利要求2所述的一种零件非喷涂面保护材料的制备方法,其特征...