Fly ash, ash and shale sintered hollow brick production formula and method. History to Qin Zhuanhan tile, the production of raw materials with lots of soil, and the destruction of natural resources and ecological balance, the lack of energy waste, the production of solid clay brick, is a large number of devouring precious arable land, cinder and ceramsite hollow brick new, strength and far from technology request, which increases the cost of building materials. Ash and Shale Fly Ash Sintered Hollow brick, formula of the invention, which comprises: fly ash, the formula also includes industrial wastes, waste shale, the weight ratio of fly ash 25 ~ 35, 25 ~ 35 of industrial waste, waste shale from 35 to 45. This product is used as building material.
【技术实现步骤摘要】
本专利技术涉及一种。
技术介绍
历史留下来的秦砖汉瓦,其制作原料需用大量的土,从而破坏自然资源和生态平衡,浪费本已缺乏的能源。目前所制作的粘土实心砖瓦,正大量吞噬着宝贵的耕地,新出现的炉灰、陶粒空心砖,强度上又远远达不到技术要求,无形中增大了建材的成本。
技术实现思路
本专利技术的目的是提供一种利用粉煤灰、炉灰及页岩烧结空心砖的配方及制作方法。上述的目的通过以下的技术方案实现粉煤灰、炉灰及页岩烧结空心砖配方,其组成包括粉煤灰,所述的配方中还包括工业废渣、废弃页岩,其重量份数比为粉煤灰25~35、工业废渣25~35、废弃页岩35~45。上述的粉煤灰、炉灰及页岩烧结空心砖的制作方法,按上述所述的重量份数比取粉煤灰、工业废渣及废弃页岩粉碎、混合,加入重量份数比为16~20的水,混合搅拌均匀,然后成型,烧结,其温度在1000℃~1100℃之间,时间为8~12小时,最后制成成品。这个技术方案有以下有益效果1.由粉煤灰、炉灰及页岩为原料烧结而成的空心砖,具有较佳的隔音效果,至少是普通建筑用砖的2倍。2.本产品具有极好的保暖效果,比普通实心砖高出3~5倍,本产品已成为最新型的最具独特优势的轻体建筑材料。3.由所选用的原料制成的空心砖无污染,取代了煤,利于环保,所采用的原料为废弃料,变废为宝,利国利民。4.本专利技术的制作方法简单,容易掌握和操作。本专利技术的具体实施例方式实施例1 ,其组成包括粉煤灰,所述的配方中还包括工业废渣、废弃页岩,其重量份数比为粉煤灰25、工业废渣25、废弃页岩35,其制作方法是按上述所述的重量份数比取粉煤灰、工业废渣及废弃页岩粉碎、混合,加入重 ...
【技术保护点】
一种粉煤灰、炉灰及页岩烧结空心砖配方,其组成包括:粉煤灰,其特征是:所述的配方中还包括工业废渣、废弃页岩,其重量份数比为粉煤灰25~35、工业废渣25~35、废弃页岩35~45。
【技术特征摘要】
【专利技术属性】
技术研发人员:张大勇,曹权安,
申请(专利权)人:张大勇,曹权安,
类型:发明
国别省市:23[中国|黑龙江]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。