The invention relates to a production method of plant fiber gypsum slag hollow block, which comprises the following steps: (1) the mixing ingredients, including plant fiber, gypsum, cement, sand or stone powder, the weight percentage of each component ingredients: plant fiber 21 - 31%, 35 - 45%, gypsum slag cement 6 8%, river sand or stone powder of 25 - 35%; (2) containing 0.8 - 1.2% additive water mixing into sticky; (3) into the block forming machine extrusion; (4) curing drying products. The method of the invention has the advantages of energy saving, low production cost, light weight of blocks and better sound insulation, heat insulation and heat preservation effect.
【技术实现步骤摘要】
本专利技术涉及建筑材料,具体涉及建筑材料的生产方法,特别是空心砌块的生产方法。
技术介绍
在我国的建筑行业中,为了使用新型建筑材料,以代替传统建材的粘土实心砖,开发研究出了用矿渣、煤渣等工业废料制作的复合墙体材料。在中国专利CN1428308“一种含植物纤维石膏砌块的配制方法”中已有记载,主要原料由石膏粉、水泥以及增强剂组成。其特征在于加入植物纤维(如棉梗、麦、稻、草、木渣)等为主要配制原料。在中国专利CN1324973“多功能砌块”文献中也有记载,由水泥、泥土、石灰、石膏、沙子、矿石粉、纤维、植物茎叶、塑料、金属等材料单独组合制成。但在这些公开专利的技术方案中,都是使用的硫酸钙含量大于80%的高纯石膏粉,不仅成本高,加工难度大,而对挖掘出来的硫酸钙含量小于60%的石膏渣没有得到充分利用,使之成为堆积成灾的废料,占用土地、污染环境。在这些技术方案中植物纤维的用量很小。而且这些技术方案的加工工艺复杂,生产成本较高,不利于新型建材的推广使用。
技术实现思路
本专利技术的目的是要提供一种具有节约能源,生产成本低廉,重量轻且有较好的隔音、隔热、保温效果的。本专利技术的技术方案是一种(1)将配料混合,配料包括植物纤维、石膏渣、水泥、河砂或石屑粉,配料各组分的重量百分比为植物纤维21-31%、石膏渣35-45%、水泥6-8%、河砂或石屑粉25-35%;(2)加入含有0.8-1.2%外加剂的水搅拌成粘稠状;(3)放入砌块成型机中挤压成型;(4)养护风干,成品。上述方案中,植物纤维为稻杆、麦杆、棉杆、树枝、谷壳、锯末中的一种或几种,植物纤维为长5-20毫米的碎屑。使用本专利 ...
【技术保护点】
一种植物纤维石膏渣空心砌块的生产方法,其特征在于:(1)将配料混合,配料包括植物纤维、石膏渣、水泥、河砂或石屑粉,配料各组分的重量百分比为:植物纤维21-31%、石膏渣35-45%、水泥6-8%、河砂或石屑粉25-35%;(2)加入含有0.8-1.2%外加剂的水搅拌成粘稠状;(3)放入砌块成型机中挤压成型;(4)养护风干,成品。
【技术特征摘要】
【专利技术属性】
技术研发人员:胡晏义,徐松如,乐传著,
申请(专利权)人:孝感市天然居墙材有限责任公司,
类型:发明
国别省市:42[中国|湖北]