镁白云石中间包干式工作衬料制造技术

本发明专利技术镁白云石中间包干式工作衬料，是一种施工方便，低温烘烤２小时后就可投入使用的不定形耐火材料。它主要由镁砂、白云石骨料与镁砂，ａ－Ａｌ↓［２］Ｏ↓［３］细粉及复合添加剂、酚醛树脂按比例混合而成。它具有抗渣侵蚀性能好，同永久衬料粘附性强，而用后清除残渣壳方便，且不损坏永久衬，使用寿命大幅提高。

Intermediate work lining of magnesia dolomite

The intermediate work type lining material for magnesium and dolomite is an unshaped refractory material which is convenient for construction and can be put into use after 2 hours of low temperature baking. It is mainly composed of magnesite, dolomite and magnesite aggregate, a Al: 2 O: 3 fine powder and composite additives, phenolic resin mixed in proportion. The utility model has the advantages of good slag corrosion resistance, strong adhesion with the permanent lining, convenient removal of the residual shell after use, and no damage to the permanent lining, and the service life is greatly improved.

【技术实现步骤摘要】

本专利技术属于耐火材料领域，更具体地说本专利技术涉及不定形耐火材料，它适用于做钢铁工业连铸中间包工作衬料。
技术介绍
在我国大力发展高效连铸的今天，中间包冶金技术日益受到重视，它已成为钢铁冶炼过程中在最后阶段最主要的精炼容器，并向大型化发展。它位于钢包与结晶器中间，因此中间包工作衬的耐火材料质量，对保证洁净炼钢，多炉连浇及中间包向大型化发展至关重要。而现普遍使用的中间包干式工作衬料，材质主要是镁质。具有使用寿命较长。施工时不加水，不用搅拌机械，低温烘烤2小时后就可使用。在烘烤过程中不爆裂，不剥落，同永久衬粘附性好，不回落坍塌，用后清除残钢渣壳容易方便，且不损坏永久衬。抗侵蚀性好。使用寿命有较大的提高。
技术实现思路
经过我们精心研究、实践、合理选择镁白云石中间包干式工作衬料各组份及配比，完成了本专利技术。本专利技术的目的是提供一种将不经烧结的白云石破碎成1mm-2mm的粒度后就直接使用的镁白云石中间包干式工作衬料，它与干式料中的其它组份，在烘烤过程中产生有利于中间包干式工作衬料应用的化学反应的一种新型干式料。它可以利用我国储量丰富价格较低的白云石替代价格较贵，资源较少的镁砂作原料，白本文档来自技高网...

【技术保护点】
镁白云石中间包干式工作衬料，其特征是其组份按重量百分比计为：白云石１ｍｍ－３ｍｍ占２０％，镁砂１ｍｍ－３ｍｍ占１２％，０．５ｍｍ－１ｍｍ占３３％；≤０．０８ｍｍ占２４％；ａ－Ａｌ↓［２］Ｏ↓［３］超微粉占５％，复合添加剂占１％；酚醛树脂占６％。以上各组份重量之和为１００％。