The invention discloses a porous ceramic material and preparation method thereof. The method comprises by weight, 5 ~ 50, 20 ~ 50 ceramic polished waste of a ceramic waste and 0 ~ 20, 0 ~ 15 ceramic clay sand, high temperature 0 ~ 15 low temperature sand mixed, according to the above raw materials the total weight of 10 to 60% to add water, and add 0 ~ 3 grinding agent and 0 to 3 portions of binder, wet milling; the material is pressed into a ceramic tile blank, sintering can be in ceramic roller kiln. The invention fully utilizes the ceramic waste material and does not need to use foaming agent to fully utilize the self foaming mechanism of the waste material of the polished brick, and the porous ceramic material prepared has the advantages of light weight, low thermal conductivity and high strength. The process is simple, the operation is easy to control, and the product has the functions of heat preservation, heat insulation, sound insulation, fire prevention and the like.
【技术实现步骤摘要】
本专利技术涉及无机材料
，具体是指。
技术介绍
随着我国城镇化、工业化进程的加快以及社会主义新农村建设的逐步展开，每年竣工的房屋建筑面积约20亿平方米。预计到2020年底，全国房屋 建筑面积将新增250至300亿平方米。但是到目前为止，几乎所有的建筑物 都不节能。节约土地、能源、淡水、矿产资源具有极端重要和紧迫的意义。我国总能耗中建筑能耗占了 30%左右(另夕卜，工业能耗占60。/。，交通能 耗占10%)。其中空调能耗占建筑能耗的50 60%，照明能耗占建筑能耗的 20 30%。如果延续目前的建筑能耗状况，预计到2020年，我国建筑业每 年将消耗1.2万亿度电和4.1亿吨标煤，接近目前全国建筑能耗的3倍，加 上建材生产能耗所占比例(16.7%)，建筑建材能耗约占全社会总能耗的 46.7%。这是一组非常可怕的数据。因此，降低建筑材料的总体生产能耗， 提高墙体材料的保温、隔热等环保性能迫在眉睫。近年来，我国陶瓷产业得到了迅猛发展，随着陶瓷产量的增加，陶瓷废 料数量越来越多。据统计，我国各种陶瓷废料总量约为1000万吨/年左右， 其中抛光砖废料量已达500万吨/...
【技术保护点】
一种多孔陶瓷材料的制备方法，其特征是，包括如下步骤和工艺条件： 第一步 以重量份数计，将５～５０份陶瓷抛光废料、２０～５０份陶瓷废料、０～２０份陶瓷粘土、０～１５份高温砂、０～１５份低温砂混合，按上述原料总重量的１０～６０％添加水，并添加０～３份助磨剂和０～３份粘结剂，进行湿法球磨； 第二步 将球磨后的物料压制成陶瓷砖坯体，在陶瓷辊道窑内烧成即可。
【技术特征摘要】
【专利技术属性】
技术研发人员：税安泽，刘艳春，夏海斌，曾令可，刘平安，程小苏，王慧，
申请(专利权)人：华南理工大学，
类型：发明
国别省市：81[中国|广州]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。