一种硅酸盐瓷质砖的制备方法技术

本发明专利技术公开了一种硅酸盐瓷质砖的制备方法。本发明专利技术包括以下步骤：（１）高温蚀硅料的制备；（２）现有硅酸盐瓷质砖所包含的面料和底料粉料的制备；（３）将各种花纹面料与高温蚀硅料并同底料一起压制成型；（４）成型后的坯体经过干燥，烧成，抛光磨边制成成品。本发明专利技术方法的采用可以采用机械化大规模生产该产品，并且经济适用，成本低廉。

Method for preparing silicate ceramic tile

The invention discloses a method for preparing a silicate ceramic tile. The invention comprises the following steps: (1) the high temperature corrosion of silicon material preparation; (2) the prior powder silicate ceramic tile contains fabric and bottom material preparation; (3) all kinds of pattern fabric and high temperature corrosion of silicon material and material together with the bottom pressing; (4) the body after molding after drying, sintering, polishing grinding of finished products. By adopting the method of the invention, the product can be produced on a large scale by mechanization, and the utility model has the advantages of economical applicability and low cost.

【技术实现步骤摘要】

本专利技术涉及一种建筑装饰用陶瓷砖的制备方法，更具体的说是涉 及一种仿天然洞石石材的硅酸盐瓷质砖的制备方法。
技术介绍
随着陶瓷行业工艺，配方，材料和装备的不断进步，陶瓷制品特 别是硅酸盐瓷质抛光砖产品越来越接近天然石材的效果，包括颜色， 质感，纹理及表面效果。近年来，表面带有管洞或凹坑的天然洞石石 材尤其受到设计师和消费者的喜爱，被大量地使用在墙面和地面的装 饰上。但这类石材价格昂贵，强度低，耐磨性差，易变色，且石材矿 物储量有限，石材荒料完全依靠进口 。而人造仿洞石瓷砖具有价格低， 强度高，经久耐用，不变色，防污性能好的优点，是天然洞石石材的 最佳替代品。目前市场上的仿洞石陶瓷砖一般是由凹凸模具压制形 成，因此表面死板固定不能象天然石材那样变化自然，近年来也有些 厂家采用发泡剂发泡成孔的方法模仿洞石，但由于发泡产生的孔洞较 小，较浅，且发泡孔洞因气泡形状为球形而导致孔口为圆形，难以表 现天然洞石石材那深管状的孔洞和变化万千的不规则洞口形状。因此，需要设计一种新的仿真天然洞石石材的陶瓷砖制备方法以 解决上述问题。
技术实现思路
本专利技术的目的在于克服现有技术存在的缺陷，提供一种本文档来自技高网...

【技术保护点】
一种硅酸盐瓷质砖的制备方法，其特征在于：包括以下步骤：　　　　（１）高温蚀硅料的制备；　　　　（２）现有硅酸盐瓷质砖所包含的面料和底料粉料的制备；　　　　（３）将各种花纹面料与高温蚀硅料并同底料一起压制成型；　　　　（４）成型后的坯体经过干燥，烧成，抛光磨边制成成品。