The invention discloses a processing method of comprehensive utilization of waste aerated concrete, aerated concrete waste and drying the anhydrous gypsum or two water gypsum calcined to mix a certain mass percentage, in the ball mill grinding system, expansive agent; the expansive agent and silicate cement mixing, prepared expansive cement. If the aerated concrete waste after calcining at high temperature, in the ball mill grinding surface area to 300 400g / cm = 2, powder, preparation of cementitious materials; the powder to the number of 50 per cubic meter 150kg as a filler or replace the lime powder filling density of concrete. The processing method of the invention is simple, and does not generate two pollution, is suitable for industrial production, makes the waste material of aerated concrete more fully utilized, and turns waste into treasure.
【技术实现步骤摘要】
本专利技术涉及建筑材料废料综合利用处理方法，具体地说是涉及一种加气混凝土废料综合利用处理方法、取代部分水泥或是自密实混凝土填料，也可与石膏质材料按一定配比混合成为膨胀剂和膨胀水泥原料。 战县仕小随着墙体保温材料在建筑领域的大力推广与使用，加气混凝土已得到工业化 生产和广泛应用。伴随而来的在建筑物拆除中产生大量的加气混凝土废弃物，而 且加气混凝土生产过程中也产生了大量的加气混凝土边角料。目前这些加气混凝 土废料多被废弃或仅仅被简单的用作填充材料，没有被有利的充分利用，浪费了 大量资源。这种传统"大量生产，大量浪费，大量废弃"的模式不符合可持续发展战略，也与2005我国两会提出的"建设节能型社会，发展循环经济"政策 相背离。提高建筑材料废弃物再生利用水平，最大限度地降低其对环境的污染， 对促进行业技术进步和实施可持续发展战略，发展绿色建材具有十分重要的理论 价值和应用价值。加气混凝土一般可以分为粉煤灰加气混凝土和石英砂加气混凝土，不含有粗 骨料，是很好的高铝含量的硅质和石灰质原料，对其进行二次再生利用具有坚实 的理论基础，有很好的社会利用经济价值。
技术实现思路
本...
【技术保护点】
一种加气混凝土废料综合利用的处理方法，其特征在于处理步骤如下：（１）首先将４０～６０％质量百分数的加气混凝土废料经１００℃～２００℃烘干１～３小时，然后与６０～４０％的无水石膏或二水石膏拌和，于球磨机内粉磨，均化即制得膨胀剂，其细度为０．０８ｍｍ，筛余：５～１０％；（２）将上述１０～３０％的膨胀剂和７０～９０％硅酸盐水泥混合均匀，即制得膨胀水泥。
【技术特征摘要】
【专利技术属性】
技术研发人员：蒋亚清，龚明子，郭莉，
申请(专利权)人：河海大学，
类型：发明
国别省市：84[中国|南京]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。