The invention relates to a method for preparing large size piezoelectric ceramics by atmosphere hot pressing sintering, which belongs to the field of piezoelectric ceramic preparation. The invention adopts ceramic mold size control, diameter 150 ~ 300mm, the mold wall thickness of 20 25mm, 100 120mm; the ceramic body into the ceramic mold, stable electric melting zirconia sand as filling in the blank around; the oxygen atmosphere atmosphere hot pressing sintering, oxygen flow in 3 - 5 liters per minute; the sintering temperature is controlled at 1220 DEG C to 1250 DEG C, keep the pressure in the 200 - 400 kg kg / cm = 2, the holding time was 4 to 12 hours, the large size prepared by pressure basic properties of piezoelectric ceramic and uniformity are good, the the preparation has not been reported before.
【技术实现步骤摘要】
本专利技术涉及一种，属于压电陶瓷 制备领域。
技术介绍
压电陶瓷换能器以其独特的性能在超声、电声、激光、导航、通讯等高技 术领域内得到了日益广泛的应用。而对于大功率换能器应用而言，不仅要求材料具有较高机电耦合系数kp 、压电常数d33的同时必须具有很低的介电损耗tan S、大的机械品质因数Qm。普通烧结工艺很难制备性能优异的大尺寸压电陶瓷， 制备过程中样品容易开裂，致密度很差，很难极化。我们采用气氛热压烧结工 艺的方法来制备大尺寸压电陶瓷。此制备工艺能大大提高材料的致密度、提高 材料的组分和结构的均匀性，提高材料的机械强度，从而降低材料的介电损耗。 大尺寸的压电陶瓷存在很多难点，普通烧结工艺很难制备出高致密、高均 匀度的大尺寸压电陶瓷，如本专利技术所述的采用气氛热压烧结法制备高致密、高 均匀度的大尺寸压电陶瓷国内还未见报道。
技术实现思路
本专利技术的目的在于提出一种气氛热压烧结大尺寸压电陶瓷的制备方法，其 步骤工序及要求如下(1)选用适合大尺寸压电陶瓷的陶瓷模具，内径尺寸控制在150-300mm， 模具壁厚20-25腿，高100-120腿。模具太小，模具的抗张强度...
【技术保护点】
气氛热压烧结制备大尺寸压电陶瓷的方法，其特征在于包括下述步骤： （１）选用大尺寸陶瓷模具，其内径尺寸控制在１５０－３００ｍｍ，模具壁厚２０－２５ｍｍ，高１００－１２０ｍｍ； （２）将陶瓷坯体放入陶瓷模具中，在坯体四周填充全稳定电熔氧化锆砂作为填料； （３）通入氧气氛进行气氛热压烧结，氧气流量控制在３－５升／分钟； （４）控制烧结温度在１２２０℃－１２５０℃，保持压力在２００－４００公斤ｋｇ／ｃｍ↑［２］，保压时间为４－１２小时。
【技术特征摘要】
【专利技术属性】
技术研发人员：仇萍荪，郑鑫森，程文秀，何夕云，曾霞，丁爱丽，
申请(专利权)人：中国科学院上海硅酸盐研究所，
类型：发明
国别省市：31[中国|上海]