Inorganic film and preparation method thereof, relating to thin film and preparation method thereof. The utility model solves the problems of complicated preparation technology, high equipment requirements, harsh film forming conditions, high cost, easy cracking and easy falling off of the existing inorganic film. Inorganic films are made from organic compounds, monomers, water, catalysts, solvents, A, solvents, B and organosilicon polymers. The preparation method comprises the following steps: preparing precursor solution of organic-inorganic hybrid film; applying the solution to the surface of the object by spraying, dipping or brushing; and then obtaining inorganic film by heat treatment. The thin film obtained by the invention has simple preparation process, easy film-forming conditions requirements on equipment, simple, low cost, anti-oxidation films can be widely applied to the metal surface, porous membrane catalyst, light-emitting films with luminescence characteristics, anti friction films, porous membranes and the structure of the sensor membrane.
【技术实现步骤摘要】
本专利技术涉及薄膜及其制备方法。技术背景无机薄膜，因其具有耐高温、化学稳定、耐腐蚀、力学强度高、结构稳定 和易于清洗再生的特点，广泛的应用在食品、饮料、医药卫生、石油化工、生 物技术、环境工程以及新型能源方面，制备无机薄膜的方法很多，最为成功的 方法之一是溶胶-凝胶法制膜，但是现有的溶胶-凝胶法制膜对因在反应过程中 对前驱体浓度、环境湿度和温度、升温制度和保温时间都有严格要求，工艺也 相当的复杂，并且对设备要求很高以及高的成本，严重限制了溶胶-凝胶法的 实际应用。
技术实现思路
本专利技术目的是为了解决现有无机薄膜的制备工艺复杂、设备要求高、成膜 条件苛刻、成本高的问题，而提供。无机薄膜由1摩尔有机化合物单体、1 6摩尔水、0.01 0.1摩尔催化剂、 3 6摩尔溶剂A、为有机化合物单体质量50% 300%的溶剂B和为有机化合 物单体质量5% 200%的有机硅高分子制成；其中溶剂A为甲醇、乙醇、异 丙醇、正丁醇、丙酮中的一种或几种，溶剂B为甲醇、乙醇、异丙醇、正丁 醇、乙酸乙酯、乙酸丁酯、丙酮中的一种或几种。无机薄膜按以下步骤制备 一、按摩尔比将1摩尔的有机化合...
【技术保护点】
无机薄膜，其特征在于无机薄膜由１摩尔有机化合物单体、１～６摩尔水、０．０１～０．１摩尔催化剂、３～１０摩尔溶剂Ａ、为有机化合物单体质量５０％～３００％的溶剂Ｂ和为有机化合物单体质量５％～２００％的有机硅高分子制成；其中溶剂Ａ为甲醇、乙醇、异丙醇、正丁醇、丙酮中的一种或几种，溶剂Ｂ为甲醇、乙醇、异丙醇、正丁醇、乙酸乙酯、乙酸丁酯、丙酮中的一种或几种。
【技术特征摘要】
【专利技术属性】
技术研发人员：王黎东，赫晓东，赵骁，
申请(专利权)人：哈尔滨工业大学，
类型：发明
国别省市：93[中国|哈尔滨]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。