The invention relates to a processing method of modified glass deepening, which can ensure the cleaning quality of the glass, improve the production quality of the glass, and can reduce the number of cleaning roller quartz furnace, greatly reduce the production cost, the technical proposal is that the original piece of glass in the cutting machine according to the requirements of cutting and grinding. Edge processing, and then edging tolerance detection, detection of qualified glass into the washing machine for cleaning, and then sent to the glass tempering furnace were tempered, and finally cleaning, the product is made of toughened glass, which is characterized in that the water used for cleaning the glass for drinking water, the drinking water is the tap water purifier.
【技术实现步骤摘要】
本专利技术涉及玻璃深化加工领域,具体为。(二)
技术介绍
一般钢化玻璃的生产工艺为玻璃原片在切割机上按要求进行切割,然后 进行磨边加工,再进行磨边公差检测,检测合格后将玻璃在清洗机内进行清洗, 然后将玻璃送至钢化炉进行钢化处理,最后再进行清洗,即得成品钢化玻璃。 此工艺的缺点在于,其清洗机内用自来水进行玻璃的清洗,由于自来水中含有 硬水盐和其他无机化合物,可与玻璃发生表面物理或化学反应,当水温高于60 'C时在清洗机里干燥后容易产生残留物,这些反应污秽表面残留物粘着力更强, 不易去除,从而导致钢化玻璃的成品缺陷,且玻璃表面的污秽残留物还能粘着 在钢化炉石英辊道上,增加了钢化炉石英辊道的清洗次数,加大了生产成本。(三)
技术实现思路
针对上述问题,本专利技术提供了,其保证玻璃 的清洗质量,提高了玻璃的生产质量,并能减少钢化炉石英辊道的清洗次数, 大大降低了生产成本。,其技术方案是这样的,玻璃原片在切割机 上按要求进行切割,然后进行磨边加工,再进行磨边公差检测,检测合格后玻 璃进入清洗机内进行清洗,然后将玻璃送至钢化炉进行钢化处理,最后再进行 清洗,即得成品钢化玻璃,其特征在于对玻璃进行清洗的水为饮用纯净水。其进一步特征在于所述饮用纯净水是由自来水净化机来制成,所述自来 水净水机包括进水管、净化系统和出水管,所述进水管内通有自来水,所述出 水管与所述清洗机内的水箱相连接。使用本专利技术工艺进行玻璃的深化加工,其有益效果在于采用纯净水进行 玻璃的清洗,能提高玻璃清洗效果,防止硬水堆积对玻璃成品造成缺陷,玻璃 的清洁能减少玻璃对钢化炉石英辊道污染,从而大幅度减少 ...
【技术保护点】
一种改良的玻璃深化加工方法,玻璃原片在切割机上按要求进行切割,然后进行磨边加工,再进行磨边公差检测,检测合格后玻璃进入清洗机内进行清洗,然后将玻璃送至钢化炉进行钢化处理,最后再进行清洗,即得成品钢化玻璃,其特征在于:对玻璃进行清洗的水为饮用纯净水。
【技术特征摘要】
【专利技术属性】
技术研发人员:冯建敏,
申请(专利权)人:无锡海达安全玻璃有限公司,
类型:发明
国别省市:32[中国|江苏]