The invention relates to a method for preparing a carbon anode for aluminum by utilizing a residual electrode, which relates to a preparation method of a carbon anode used for aluminum, in particular to a method for producing a carbon anode for aluminum by using the residual pole as the main raw material. It is characterized in that the preparation process of carbon anode for aluminium scrap, ash less than 0.8%, the sodium content of less than 600ppm, the residual anode in the anode production process of blending proportion can be accounted for 30% of the 100% dry. The invention widens the selection range of the raw material of the carbon anode by using a large number of low cost residues, and is favorable for maintaining the sustainability of the production of the carbon anode and reducing the manufacturing cost of the carbon anode.
【技术实现步骤摘要】
一种利用残极制备铝用炭阳极的方法,涉及一种铝用炭阳极生产制备,特别是以残极作为主要原料制作铝用炭阳极的方法。技术背景铝电解用炭阳极是有煅后石油焦和煤沥青经过混捏成型和高温焙烧制作而成,有的企业也加入残极作为原料。残极是预焙阳极在电解槽上使用后被换下的残余部分,由于其含有较高的杂质,一般其在炭阳极中生产中使用的比例不超过30%。残极和煅后焦一起称为干料。近几年,随着铝工业的快速发展,适用于铝用炭素的石油焦越来越少,石油焦质量恶化,硫含量增高,价格上升,迫使企业寻找新的原料代替石油焦;铝工业模式也发生了一些变化,之前大多数电解厂有配套的碳素厂,市场没有商品阳极,也就是独立的碳素厂,电解厂的残极会返回碳素厂,作为原料继续生产阳极。现在商品阳极的出现,电解厂和碳素厂的分离导致了大量残极无法消化,残极只能作为一种低附加值的产品出售,导致资源的浪费。目前,新疆地区新建了数个大规模的电解铝企业,而无配套的碳素厂,大量残极运回内地加工消化,运输成本极大,而且,新疆地区缺乏石油焦资源,石油焦由内地运入成本较高,使用高比例残极制备铝用炭阳极,既能就地消化电解厂产生的残极,又能避免使用成本高的石油焦,降低了炭阳极的制作成本。因此,迫切需要研究在炭阳极中提高提高残极使用比例的技术。
技术实现思路
本专利技术的目的就是针对上述已有技术存在的不足,提供一种能有效应对石油焦质量不断恶化的现状,高效利用残极,降低铝用炭阳极成本的方利用残极制备铝用炭阳极的方法。本专利技术的目的是通过以下技术方案实现的。一种利用残极制备铝用炭阳极的方法,其特征在于在炭阳极制备过程中,掺配残极的用量占干料比 ...
【技术保护点】
一种利用残极制备铝用炭阳极的方法,其特征在于在炭阳极制备过程中,掺配残极的用量占干料比例为30%‑100%。
【技术特征摘要】
1.一种利用残极制备铝用炭阳极的方法,其特征在于在炭阳极制备过程中,掺配残极的用量占干料比例为30%-100%。2.根据权利要求1所述的一种利用残极制备...
【专利技术属性】
技术研发人员:寇帆,陈开斌,罗英涛,苏自伟,胡聪聪,张劲斌,
申请(专利权)人:中国铝业股份有限公司,
类型:发明
国别省市:北京;11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。