The invention discloses a galvanized metal polishing agent, to the quality of a project, including the following ingredients: glycerin monostearate 8 15 hydroxy ethylidene phosphonic acid two, 9, 4 monoethanolamine 6 10 copies, 12 copies, 6 butanol sodium succinate 12 18 and water glass 3 6 copies, 150 copies of 120 deionized water. Methods using galvanized metal polishing agent said: 1) glycerin monostearate, two hydroxy ethylidene phosphonic acid, monoethanolamine, butanol, sodium succinate, water glass in the deionized water, heating, the temperature is 50 60 DEG C, stirring evenly; 2) the galvanized metal the surface of sandpaper and sandblasting; 3) step 1) into 50 pieces of galvanized metal processing 60 DEG C into the polishing agent, time is 10 20min; 4) the galvanized metal piece out and cooling immediately after cleaning.
【技术实现步骤摘要】
本专利技术涉及金属表面处理
,具体涉及一种镀锌金属抛光剂及其使用方法。
技术介绍
金属表面抛光因能降低金属制品表面粗糙度,具有增加金属制品光泽度和消除锈迹等优点,但现有用于镀锌金属件的抛光剂产品存在抗腐蚀性能差,稳定性差,处理时间较长等问题。
技术实现思路
本专利技术的目的是为了解决现有技术的不足,提供一种镀锌金属抛光剂及其使用方法,制得的抛光剂尤其适用于镀锌钢件,抗抗腐蚀性能强,稳定性好。本专利技术采用如下技术方案:一种镀锌金属抛光剂,以质量份计,包括如下原料:甘油单硬酯酸酯8-15份、羟基乙叉二膦酸4-9份、单乙醇胺6-10份、丁醇6-12份、琥珀酸钠12-18份、水玻璃3-6份、去离子水120-150份。本专利技术还提供一种镀锌金属抛光剂的使用方法,具体步骤为:1)将甘油单硬酯酸酯、羟基乙叉二膦酸、单乙醇胺、丁醇、琥珀酸钠、水玻璃依次加入去离子水中,加热,温度为50-60℃,搅拌均匀;2)将待处理的镀锌金属件表面进行砂纸磨平和喷砂处理;3)将步骤1)处理的镀锌金属件放入50-60℃的抛光剂,放入时间为10-20min;4)将镀锌金属件取出,降温清洗后即可。本专利技术的有益效果为:本专利技术抛光剂不仅能够有效的去除镀锌金属表面的油污和锈斑,使其表面光泽明亮,而且本专利技术组分中的甘油单硬酯酸酯、羟基乙叉二膦酸有效提高镀锌金属件的抗腐蚀性能。具体实施方式下面结合实施例对本专利技术作进一步的详细描述。实施例1一种镀锌金属抛光剂,以质量份计,包括如下原料:甘油单硬酯酸酯12份、羟基乙叉二膦酸7份、单乙醇胺9份、丁醇10份、琥珀酸钠16份、水玻璃5份、去离 ...
【技术保护点】
一种镀锌金属抛光剂,其特征在于,以质量份计,包括如下原料:甘油单硬酯酸酯8‑15份、羟基乙叉二膦酸4‑9份、单乙醇胺6‑10份、丁醇6‑12份、琥珀酸钠12‑18份、水玻璃3‑6份、去离子水120‑150份。
【技术特征摘要】
1.一种镀锌金属抛光剂,其特征在于,以质量份计,包括如下原料:甘油单硬酯酸酯8-15份、羟基乙叉二膦酸4-9份、单乙醇胺6-10份、丁醇6-12份、琥珀酸钠12-18份、水玻璃3-6份、去离子水120-150份。2.根据权利要求1所述的镀锌金属抛光剂的使用方法,其特征在于:1)将甘油单...
【专利技术属性】
技术研发人员:苏建丽,
申请(专利权)人:青岛文创科技有限公司,
类型:发明
国别省市:山东;37