The production method of the invention discloses a rubber strip type insulating glass, which comprises the following steps: design and optimization of glass cutting, grinding of glass and glass cleaning drying, hollow glass assembly, glass sheet, inspection, packing and storage, which is characterized in that the temperature of the glass in the hot press, the 85 95 C, time is 90 100 seconds, at the end of two outer spacer coating sealant. The invention adopts new technology, and then at a distance of a lateral coated hollow glass sealant, the sealing effect is better, the probability of gas leakage and water vapor into the hollow glass of a decrease, increase the safety performance of hollow glass.
【技术实现步骤摘要】
本专利技术涉及中空玻璃
，具体涉及一种胶条式中空玻璃的生产方法。
技术介绍
随着国内玻璃加工行业的发展以及人们对中空玻璃的优点性能认识的不断深入，中空玻璃的应用范围在不断扩大，除在玻璃幕墙、汽车、飞机等方面得到广泛应用外，目前已开始进入寻常百姓家。这主要是由于中空玻璃的应用能改善建筑物的隔热和隔音效果的同时，简化了空调等通风保暖设施的结构设计，这不仅降低了建筑装饰费用而且实际增加了建筑物内的有效实用空间。
目前国内市场上比较常见的有两种中空玻璃：1、铝条式中空玻璃：此种中空玻璃80年代引入，相对成熟些，但是加工工艺较复杂；2、胶条式中空玻璃：此种中空玻璃在国内刚刚起步，但是制造工艺简单，因此应用范围广，推广很快，但中空密封效果不佳。
中空玻璃的应用在不断的扩大，人们对中空玻璃的质量要求也越来越高。但是，随着时间的推移，中空玻璃上的密封胶可能会发生破裂、老化等现象，就会造成中空玻璃气体泄露和水汽进入，密封层失效后玻璃的承载性能明显降低，影响中空玻璃的安全使用。
技术实现思路
本专利技术提供一种胶条...
【技术保护点】
一种胶条式中空玻璃的生产方法，包括以下步骤：玻璃设计优化及切割下料、玻璃磨边及玻璃清洗干燥、中空玻璃组装、玻璃合片压片、封胶、检验、包装、入库，其特征在于：玻璃在热压机时的温度为85‑95℃，时间为90‑100秒，最后在间隔条外侧涂二道密封胶。
【技术特征摘要】
1.一种胶条式中空玻璃的生产方法，包括以下步骤：玻璃设计优化及切割下料、玻璃磨边及玻璃清洗干燥、中空玻璃组装、玻璃合片压片、封胶、检验、包装、入库，其特征在于：玻璃在热压机时的温度为85-95℃，时间为90-100秒，最后在间隔条外...