The invention relates to the field of low temperature plastic, discloses a low-temperature impact resistant plastic, made from the following raw materials in weight portion: 32 by polyhexamethylene adipamide 38 copies, 17 copies, 12 Teflon glass fiber 10, 5 polysulfone resin 8 12 phthalate two isodecyl formate two 5 8 copies, 14 copies of 10 trimethyl borate, ultra high molecular weight polyethylene 16 19 copies, 7 copies, 5 calcium carbonate antibacterial agent 3 9 copies, 14 copies of 8 silane crosslinking agent. The invention provides a low temperature resistant and impact resistant plastic, which improves the tolerance, toughness and impact resistance of plastic in low temperature environment.
【技术实现步骤摘要】
一种耐低温抗冲击塑料
本专利技术涉及低温塑料领域,特别是涉及一种耐低温抗冲击塑料。
技术介绍
塑料,是指以高分子量的合成树脂为主要组分,加入适当添加剂,如增塑剂、稳定剂、阻燃剂、抗菌剂、着色剂等,经加工成型的塑性(柔韧性)材料,或固化交联形成的刚性材料。随着塑料的用途越来越广泛,塑料用品的种类也越来越多。由于塑料自身所展现的诸如质量轻,优良的化学稳定性和电绝缘性及热的不良导体等性能,使塑料的应用领域和地域越来越宽泛。目前使用的塑料制品的使用温度范围比较窄,不能满足需求。在深冷领域、生物领域、食品领域、医药领域会使用到低温液体用于低温处理或保存物品,例如生产中用到的储存液氨用塑料容器、冻存管、冻存架、低温手套等。
技术实现思路
本专利技术旨在提供一种耐低温抗冲击塑料,以解决现有技术中的上述问题。本专利技术采用的技术方案为:一种耐低温抗冲击塑料,由以下重量份的原料制成:聚己二酸己二胺32-38份、聚四氟乙烯12-17份、玻璃纤维5-10份、聚砜类树脂8-12份、邻苯二甲酸二异癸酯5-8份、硼酸三甲酯10-14份、超高分子量聚乙烯16-19份、碳酸钙5-7份、抗菌剂3-9份、硅烷交联剂8-14份。优选的,一种耐低温抗冲击塑料,由以下重量份的原料制成:聚己二酸己二胺36份、聚四氟乙烯15份、玻璃纤维10份、聚砜类树脂10份、邻苯二甲酸二异癸酯7份、硼酸三甲酯13份、超高分子量聚乙烯18份、碳酸钙7份、抗菌剂8份、硅烷交联剂13份。本专利技术的有益效果是:本专利技术所采用原料均为常见的化工原料,生产成本低,市场竞争力强。更重要的是,提高了塑料在低温环境下的拉伸强度和断裂 ...
【技术保护点】
一种耐低温抗冲击塑料,其特征在于,由以下重量份的原料制成:聚己二酸己二胺32‑38份、聚四氟乙烯12‑17份、玻璃纤维5‑10份、聚砜类树脂8‑12份、邻苯二甲酸二异癸酯5‑8份、硼酸三甲酯10‑14份、超高分子量聚乙烯16‑19份、碳酸钙5‑7份、抗菌剂3‑9份、硅烷交联剂8‑14份。
【技术特征摘要】
1.一种耐低温抗冲击塑料,其特征在于,由以下重量份的原料制成:聚己二酸己二胺32-38份、聚四氟乙烯12-17份、玻璃纤维5-10份、聚砜类树脂8-12份、邻苯二甲酸二异癸酯5-8份、硼酸三甲酯10-14份、超高分子量聚乙烯16-19份、碳酸钙5-7份、抗菌剂3-9份、硅烷交...