The invention belongs to the field of metal surface treatment technology, in particular relates to a magnesium alloy micro arc oxidation electrolyte. The materials ratio is: 5 15g/L sodium hydroxide, sodium perborate potassium fluoride 4 20g/L 3, 15g/L, ZX 1 2 additives 10g/L. The invention provides electrolyte to meet the application requirements of micro arc oxidation for magnesium alloy, reduces arcing voltage, and solves surface treatment problems of complex workpieces, small workpieces and workpieces needing repairing. ZX added 1 additives can significantly reduce the arc voltage, the voltage control in the safe voltage range, and the lower the arcing voltage, the same time micro film more thick, can enhance the corrosion resistance of micro arc oxidation film and uniformity.
【技术实现步骤摘要】
一种镁合金微弧氧化电解液
本专利技术属于金属表面处理
,具体涉及一种镁合金微弧氧化电解液。
技术介绍
镁合金微弧氧化由于良好的耐蚀性能,耐磨性及原位生长等特性,越来越成为镁合金高端防腐的首选工艺,尤其是对工件有高精度要求的产品,微弧氧化由于其原位生长特性,不会影响工件精度。越来越受到人们的欢迎。随着微弧氧化技术的逐步应用,需要处理的工件由原来的结构相对简单的工件向复杂结构件改变,大面积工件向小工件转变。目前一种镁合金微弧氧化机,解决了复杂工件、小工件及返修工件的表面氧化处理问题,这种镁合金微弧氧化机,需要一种微弧氧化电解液,来满足工件表面的使用要求。
技术实现思路
本专利技术要解决的技术问题是,提供一种电解液,满足镁合金微弧氧化机使用要求,降低起弧电压,解决复杂工件、小工件、需要修补工件的表面处理问题。为解决上述技术问题,本专利技术提供的电解液,用料配比为:氢氧化钠5-15g/L,过硼酸钠3-20g/L,氟化钾4-15g/L,添加剂ZX-12-10g/L,其余组分为水。优选地,所述添加剂ZX-1的组成为:丙三醇0.5-1.5g/L,三乙醇胺0.5-1.0g/L,过硼酸纳1-2g/L,其余组分为水。优选地,电解液使用温度不超过45℃。优选地,电解液的用料配比为:氢氧化钠9g/L,过硼酸钠10g/L,氟化钾10g/L,添加剂ZX-13g/L。优选地,所述添加剂ZX-1的用料为:丙三醇1g/L,三乙醇胺0.8g/L,过硼酸纳1.5g/L。本专利技术的有益效果与现有技术相比较,本专利技术具备如下有益效果:解决复杂工件、小工件、需要修补工件的表面处理问题。利用小型 ...
【技术保护点】
一种镁合金微弧氧化电解液,其特征在于,用料配比为:氢氧化钠5‑15g/L,过硼酸钠3‑20g/L,氟化钾4‑15g/L,添加剂ZX‑1 2‑10g/L,其余组分为水。
【技术特征摘要】
1.一种镁合金微弧氧化电解液,其特征在于,用料配比为:氢氧化钠5-15g/L,过硼酸钠3-20g/L,氟化钾4-15g/L,添加剂ZX-12-10g/L,其余组分为水。2.根据权利要求1所述的电解液,其特征在于,所述添加剂ZX-1的组成为:丙三醇0.5-1.5g/L,三乙醇胺0.5-1.0g/L,过硼酸纳1-2g/L,其余组分为水。3...