The invention discloses a tube material wear line for PVC shielding heating cable, its main raw material includes: diameter 0.1 ~ 0.2mm PVC resin, two formic acid and two phthalate dioctyl phthalate two formic acid and two benzene grease, Yuan bromobenzene, nano inorganic flame retardant. The preparation method of the threading pipe shielding performance, shielding layer can replace the heating cable, which reduces the preparation cost of heating cable, conduit combustion performance test oxygen index >40, meet the safety requirements. Meanwhile, the mechanical indexes such as bending resistance, impact resistance and compressive resistance of the threading pipe made by the invention meet the requirements of use.
【技术实现步骤摘要】
—种用于发热电缆的PVC屏蔽穿线管材料
本专利技术涉及一种穿线管,具体涉及一种用于发热电缆的PVC屏蔽穿线管材料。
技术介绍
发热电缆是近年来进入我国的一种以供暖为目的、通电后能够发热的电暖,是电采暖产品,发热电缆由冷线和热线相接起来的,其中,热线是由绝缘层、接地线、屏蔽层和外护套组成,发热电缆通电后,热线发热,并在40~60°C的温度间运行,埋设在填充层内的发热电缆,将热能通过热传导(对流)的方式和发出的7_14um的远红外线辐射方式传给受热体。发热电缆在室外用于工业领域时需经常使用穿线管,此时对穿线管的阻燃和屏蔽性能要求较高。穿线管按阻燃可分为有卤阻燃和无卤阻燃两种类型,其中,有卤阻燃虽然添加量小、阻燃性能高,但其燃烧时会挥发出大量的有毒烟气,造成“二次灾害”。无卤阻燃材料的基体一般是金属氧化物、金属有机化合物、水合金属氢氧化物等,阻燃剂是氢氧化镁、氢氧化铝、三氧化二锑、钥的化合物等。如果阻燃剂配方不合理,阻燃效果不太理想,若通过增加添加量来提高阻燃性能的话,又会提高了产品的成本和影响了材料的弯折性能,难以达到国家标准的规定。另外,现有发热电缆需设置单独的屏蔽层,屏蔽层大多为复膜铝箔材料、复膜铜箔材料或编织铜网,这无疑提高了发热电缆的制备成本。
技术实现思路
本专利技术的目的在于针对现有技术的不足,提供一种用于发热电缆的PVC屏蔽穿线管材料,由于使用该材料制备的穿线管具有良好的屏蔽功能,因而可替代发热电缆的屏蔽 层。本专利技术的上述目的是通过如下方案实现的:一种用于发热电缆的PVC屏蔽穿线管材料,所述屏蔽穿线管材料由下述重量份的原料组成:粒径为 ...
【技术保护点】
一种用于发热电缆的PVC屏蔽穿线管材料,其特征在于,所述屏蔽穿线管材料由下述重量份的原料组成:FDA0000389147730000011.jpg
【技术特征摘要】
1.一种用于发热电缆的PVC屏蔽穿线管材料,其特征在于,所述屏蔽穿线管材料由下述重量份的原料组成: 粒杼为0.1~0.2mm的聚氯乙烯树脂 100~200份邻苯二甲酸二辛脂10~30份邻苯二甲酸二苯脂10~30份元溴苯10~20份氯化聚乙烯IO~20份粒径为300~500目的碳酸钙10~30份 冲击改性剂ACR5~15份 复合铅盐稳定剂5~15份 氧化聚乙烯蜡0.5~2份纳米级无机阻燃剂5~15份。2.根据权利要求1所述的一种用于发热电缆的PVC屏蔽穿线管材料,其特征在于,所述屏蔽穿线管材料由下述重量份的原料组成:粒径为0.1~0.2mm的聚氯乙烯树脂 150份邻苯二甲酸二辛脂20份邻苯二甲酸二苯脂20份元溴苯1...