The invention discloses a textile bobbin alloy material for high processability, which is characterized in that includes the following parts by weight: 100 portions of PVC resin; ABS resin 20-30; pigment 10-25, rosin resin acid 10-19, fatty acid salts of 14-24, nano calcium sulfate 14-21, titanate coupling agent 8-16, nano silver 0.5, maleic anhydride grafted polypropylene 1-3, waterborne defoaming agent 1-2, IPN emulsion 1-5. The comprehensive physical and mechanical performance is good, the tensile strength, bending strength, impact strength and heat distortion temperature and other quality indicators have reached the high strength textile bobbin and outdoor seating and refrigerator door product requirements.
【技术实现步骤摘要】
一种高成型加工性的纺织纱管合金材料
本专利技术涉及一种高成型加工性的纺织纱管合金材料。
技术介绍
随着PVC加工技术的发展，对PVC的改性研究越来越显得重要。国际上，在改性PVC材料中，PVCjABS材料是开发较早、应用基础研究较为深入的品种。已逐步成为一种性能优良有较强市场竞争力的新型材料。PVCABS合金材料既具有PVC的耐腐蚀性、高刚性、阻燃和电绝缘性好等优点，又兼有ABS的成型加工性、抗冲击性好等优点，是一种较为理想的材料。
技术实现思路
本专利技术所要解决的技术问题是提供一种高成型加工性的纺织纱管合金材料。为解决上述技术问题，本专利技术采用的技术方案是: 一种高成型加工性的纺织纱管合金材料，其特征在于，包括下列重量份数的物质:pvc树脂100份；ABS树脂20-30份；颜料10_25份，松香基树脂酸10-19份，高级脂肪酸盐14-24份，纳米硫酸钙14-21份，钛酸酯偶联剂8-16份，纳米银0.5份，马来酸酐接枝聚丙烯1_3份，水性消泡剂1-2份，网络互穿乳液1-5份。本专利技术的有益效果是:具有较好的物理、机械综合性能，其拉伸强度、弯曲强度、缺口冲击强度和热变型温度等质量指标达到高强度纺织纱管、室外座椅和冰箱门框产品的要求。【具体实施方式】实施例1 一种高成型加工性的纺织纱管合金材料，其特征在于，包括下列重量份数的物质:pvc树脂100份；ABS树脂20-30份；颜料10_25份，松香基树脂酸10-19份，高级脂肪酸盐14-24份，纳米硫酸钙14-21份，钛酸酯偶联剂8-16份，纳米银0.5份，马来酸酐接枝聚丙烯1_3份，水性消泡...
【技术保护点】
一种高成型加工性的纺织纱管合金材料，其特征在于，包括下列重量份数的物质：PVC树脂100份；ABS树脂20?30份；颜料10?25份，松香基树脂酸10?19份，高级脂肪酸盐14?24份，纳米硫酸钙14?21份，钛酸酯偶联剂8?16份，纳米银0.5份，马来酸酐接枝聚丙烯1?3份，水性消泡剂1?2份，网络互穿乳液1?5份。
【技术特征摘要】
1.一种高成型加工性的纺织纱管合金材料，其特征在于，包括下列重量份数的物质:PVC树脂100份；ABS树脂20-30份；颜料10-25份，松香基树脂酸10_19份...