环保防腐蚀涂料制造技术

本发明专利技术公开了一种环保防腐蚀涂料，由以下重量份的成分组成：双酚A型环氧树脂30～50；丁基橡胶5～10；阻燃剂10～15；二甲基乙醇胺1～2；三聚磷酸铝10～20；增稠剂10～15；石蜡3～5；氯化锌1～3；去离子水10～15。该涂层在常温酸、碱、盐溶液、汽油、煤油、柴油、水的混合液中长期浸泡无变化。使用寿命长，可广泛应用于原油、煤油、汽油等储油罐及输油管线内壁，也可适用于化工设备、管线的内壁防腐。

Environmental protection anticorrosive coating

The invention discloses an environment-friendly anti-corrosion coatings, consists of the following components: weight of bisphenol A type epoxy resin 30 ~ 50, 5 ~ 10; butyl rubber; flame retardant 10 ~ 15; two monomethylethanolamine 1 ~ 2 and 10 ~ 20; aluminum tripolyphosphate; thickening agent 10 ~ 15; 3 paraffin 5 ~ 1 ~ 3; zinc chloride; deionized water from 10 to 15. The coating has no long-term change in the mixture of acid, alkali, salt solution, gasoline, kerosene, diesel oil and water. The utility model has the advantages of long service life, and can be widely applied to oil storage tanks such as crude oil, kerosene, gasoline and the inner wall of the oil pipeline, and also can be applied to the inner wall corrosion prevention of chemical equipment and pipelines.

【技术实现步骤摘要】

【技术保护点】
一种环保防腐蚀涂料，其特征在于，由以下重量份的成分组成：双酚A型环氧树脂?????????????????????30～50；丁基橡胶?????????????????????????????5～10；阻燃剂???????????????????????????????10～15；二甲基乙醇胺?????????????????????????1～2；三聚磷酸铝???????????????????????????10～20；增稠剂???????????????????????????????10～15；石蜡?????????????????????????????????3～5；氯化锌???????????????????????????????1～3；去离子水?????????????????????????????10～15。

【技术特征摘要】

【专利技术属性】
技术研发人员：孙梁博，王岐山，
申请(专利权)人：青岛博玉特橡塑制品有限公司，
类型：发明
国别省市：