The invention provides an aluminum flake powder coating production method is the use of nitrogen and aluminum reaction was characteristic of the liquid and play a protective role in the process of grinding into powder under high pressure at room temperature, the powder and liquid nitrogen into the vibration grinding grinding flake, the vortrap isolated aluminum flake powder of different grain sizes the filtered separate most of liquid nitrogen in the container, and then injected into the dry air and control the oxygen content is less than 4%, the aluminum flake powder under the protection of nitrogen and oxygen content less controlled reaction, the surface activity of high alumina film formed completely and have protective effect, become the whole aluminum flake powder coating; the production process is in a closed environment in the continuous production of nitrogen protection, no waste discharge and volatile substances.
【技术实现步骤摘要】
【专利摘要】本专利技术提供一种片状铝粉粉末涂料生产方法，是利用不与铝粉反应的氮气在高压常温下呈液态并在铝粉研磨成片过程中起保护作用的特性，把铝粉和液氮放进振动磨研磨成片状铝粉后，通过旋流分级器分离出不同粒度规格的片状铝粉，经过过滤分离出大部分液氮，再在容器内注入干燥的空气并控制氧含量＜4％，使片状铝粉在氮气保护下与较小含量的氧气有控制的反应，表面完全形成活性高并有保护作用的氧化铝膜后，就成为片状铝粉粉末涂料；整个生产流程是在有氮气保护的封闭环境内连续生产，没有挥发性物质排出和废弃物产生。【专利说明】
本专利技术为，属于金属颜料
。
技术介绍
现片状铝粉粉末涂料的生产方法是先用油类溶剂与铝粉混合在球磨机里进行湿法研磨，使铝粉成为片状并与溶剂混合在一起，然后用振动筛和压滤机分离出大部分溶剂，再用不与铝粉反应的挥发性化学溶剂(丙酮等)洗去油性溶剂，待湿的片状铝粉分散开，挥发性化学溶剂挥发后就成为片状铝粉的粉末涂料。这种片状铝粉的生产方式不连续，采用球磨机研磨产量较低、研磨时间长、能耗高，而且成品率较低；有挥发易燃的溶剂，产生污染环境的化学品挥发物排放...
【技术保护点】
一种片状铝粉粉末涂料生产方法，其特征在于铝粉与液氮按照比例放入振动磨内，在高压常温状态研磨成液氮与片状铝粉的混合物，通过旋流分级器把不同细度的片状铝粉分开成为不同规格的产品，再分别进入固液分离器使大量液氮与片状铝粉分离，把带有少量液氮的片状铝粉输入铝粉氧化控制容器中，在容器中输入干燥的空气并控制含氧量小于4％，片状铝粉在有氮气保护的容器中与较小含量的氧气有控制反应，在表面完全形成氧化铝膜后，就成为片状铝粉粉末涂料。
【技术特征摘要】