The invention discloses a method for preparing AB3 type hydrogen storage alloy composite electrode material and application thereof. Under the protection of argon, by vacuum induction melting metal prepared AB3 alloy, alloy by mechanical grinding, milling and screening 200~300 alloy powder; the alloy powder and 200~300 type AB5 alloy MlNi3.5Co0.6Mn0.4Al0.5 powder with a mass ratio of 9.0:1.0 or 9.5: 0.5 after mixing / 200~250 in planetary mill minutes the speed of milling 60~90 minutes to form a composite alloy powder, powder and carbonyl nickel composite alloy in a weight ratio of 1:2 grinding 8~12 minutes after mixing, pressing on the desktop electric tablet machine, which is made of AB3 type hydrogen storage alloy composite electrode materials, applied to the development of power battery Ni/MH battery anode materials. The invention can improve the cycle stability and the dynamic performance of the AB3 alloy by compound treatment.
【技术实现步骤摘要】
本专利技术涉及冶金科学以及电化学研究领域，特别涉及对作为动力型Ni/MH电池负极材料的AB3型储氢合金Laa35Pra3ciMga35N^9tlAla3tl进行复合改性处理，以提高其综合性倉泛。
技术介绍
储氢合金在Ni/MH 二次电池中的应用最广泛，其中最早应用于产业化的是AB5型储氢合金，该类合金具有电化学综合性能良好、成本低等优点，但因受到合金晶体结构(CaCu5型)的限制，其放电容量仅为30(T320mAh/g，接近其理论容量348mAh/g，难以进一步提高其容量，因而不能适应Ni/MH动力电池进一步提高能量密度的发展要求；研究发现，AB3型合金的储氢容量高于AB5型稀土系储氢合金,达到36(T410mAh/g,且对环境友好,被认为是最具潜力的储氢材料，但AB3型合金表面的La和Mg极易受强碱性电解液腐蚀和氧化，生成没有储氢性能的氢氧化物和氧化物，同时在连续的充放电过程中，合金成分发生较大的体积膨胀而粉化，导致合金的循环稳定性能很差，因此，提高AB3型储氢合金的循环稳定性能成为了研究热点；通过与具有优异循环稳定性能的AB5型合金复合，以达到提高AB3型合...
【技术保护点】
一种AB3型储氢合金复合电极材料的制备方法，其特征在于具体步骤为：(1)按照目标产物摩尔配比称取纯度为99%以上的金属原料，在氩气保护下通过真空感应熔炼制备出AB3?型合金La0.35Pr0.30Mg0.35Ni2.90Al0.30，将所制得的合金机械粉碎后，在行星式球磨机上以225~250?转/分钟的转速球磨?30~60分钟，然后筛分出200~300目的合金粉末用于后续复合处理；(2)将步骤(1)筛分出的200~300目的合金粉末与200~300目的AB5型合金MlNi3.5Co0.6Mn0.4Al0.5粉末以质量比9.0:1.0或者9.5:0.5混合后，在行星式球磨机上...
【技术特征摘要】
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。