一种钢包用铬质引流砂及其制备方法技术

本发明专利技术涉及一种钢包用铬质引流砂及其制备方法。其技术方案是：先将50～70wt％的铬矿砂和20～40wt％的石英砂加入搅拌机中，搅拌2～3分钟；再将5～10wt％的钾长石加入该搅拌机中，搅拌5～10分钟；然后将1～2wt％的鳞片石墨加入该搅拌机中，搅拌10～15分钟；最后将搅拌均匀的四种物料从该搅拌机中倒出，在180～220℃条件下烘烤30～40min，即得钢包用铬质引流砂。本发明专利技术所制备的钢包用铬质引流砂具有耐火度高、高温烧结性能好、抗钢水和熔渣侵蚀性好、颗粒粒度分布均匀、流动性好、热膨胀率较小、成本适宜和自开率高的特点。

Chromium containing drainage sand for steel ladle and preparation method thereof

The invention relates to a chromium drainage sand for a ladle and a preparation method thereof. The technical scheme is: 50 ~ 70wt% chrome ore and 20 ~ 40wt% quartz sand is added into the mixer, stir for 2 to 3 minutes; then 5 ~ 10wt% potassium feldspar added to the mixer, stirring for 5 to 10 minutes; then 1 ~ 2wt% flake graphite is added to the mixer, mixing 10 ~ 15 minutes; finally mixing four materials evenly poured from the mixer, in 180 ~ 220 Deg. C bake for 30 ~ 40min, the ladle drainage sand chrome. The prepared by chrome ladle drainage sand with high refractoriness, high temperature resistance, good sintering properties of molten steel and slag erosion resistance, uniform particle size distribution, good fluidity, thermal expansion and cost for the self open rate high characteristic, small rate.

【技术实现步骤摘要】

本专利技术属于引流砂
，具体涉及。
技术介绍
随着世界经济的发展和科学技术的进步，社会各个领域对钢材的质量提出了更高 的要求。钢铁企业内“精品钢材理念”不断深化，国内大型钢厂在提高钢铁产量的同时，更 加注重高规格品种钢的生产。连铸和炉外精炼的发展使得生产效率得到了提高，但同时出钢温度变得更高，钢 水传搁时间变得更长，传统的塞棒系统已经很难满足要求，取而代之的则是钢包水口系统。精炼钢包在浇钢时如果不能自动开浇，会有一部分钢水敞开浇注，发生二次氧化， 同时将夹杂物带入结晶器中，使铸坯表面出现裂纹、夹杂等缺陷，降低了铸坯的质量，这对 高规格品种钢的生产尤为不利。因此，生产高质量的钢，必须要求钢包能自动开浇，理想化 状态是钢包自动开浇率达到100%。钢包自动开浇率和以前相比，都有很大程度的提高，开 浇率甚至达到了 99%以上，但还是会出现不自开的情况，因此提高钢包自动开浇率迫在眉 睫。目前国内外使用的引流砂以锆质引流砂、铬质引流砂、硅质引流砂和镁质引流砂 为主，其中各大钢厂普遍使用的为硅质引流砂和铬质引流砂。硅质引流砂主要由石英砂和碱性长石制成，同时也添加了适量的碳黑等含碳物质 和本文档来自技高网...

【技术保护点】
１．一种钢包用铬质引流砂的制备方法，其特征在于先将５０～７０ｗｔ％的铬矿砂和２０～４０ｗｔ％的石英砂加入搅拌机中，搅拌２～３分钟；再将５～１０ｗｔ％的钾长石加入该搅拌机中，搅拌５～１０分钟；然后将１～２ｗｔ％的鳞片石墨加入该搅拌机中，搅拌１０～１５分钟；最后将搅拌均匀的四种物料从该搅拌机中倒出，在１８０～２２０℃条件下烘烤３０～４０ｍｉｎ，即得钢包用铬质引流砂。

【技术特征摘要】

【专利技术属性】
技术研发人员：赵惠忠，刘锋，余俊，张寒，陶博，袁聪，
申请(专利权)人：武汉科技大学，
类型：发明
国别省市：83